Review on the thermo-oxidative degradation of polymers during processing and in service

被引：0
作者：
Gijsman, Pieter [1 ,2 ]
机构：
[1] DSM Res & Patents, SRU Performance Mat, NL-6160 MD Geleen, Netherlands
[2] Eindhoven Univ Technol, Dept Chem Engn, Lab Polymer Technol, NL-5600 MB Eindhoven, Netherlands
来源：
E-POLYMERS | 2008年
关键词：
D O I：
暂无
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
During processing as well as in service life, polymers degrade. For the majority of polymers this is due to oxidative processes. In this review the mechanism of the thermo-oxidative degradation of the most important (unstabilized) polymers as well as the factors determining the degradation rates are discussed.
引用
收藏
页数：34
相关论文
共 174 条
  • [1] Evaluation of the influence of various (ether, ketone and sulfone) groups on the apparent activation energy values of polymer degradation
    Abate, L
    Blanco, I
    Orestano, A
    Pollicino, A
    Recca, A
    [J]. POLYMER DEGRADATION AND STABILITY, 2003, 80 (02) : 333 - 338
  • [2] The isothermal degradation of some polyetherketones: a comparative kinetic study between long-term and short-term experiments
    Abate, L
    Blanco, I
    Motta, O
    Pollicino, A
    Recca, A
    [J]. POLYMER DEGRADATION AND STABILITY, 2002, 75 (03) : 465 - 471
  • [3] On a transition at 80°C in polypropylene oxidation kinetics
    Achimsky, L
    Audouin, L
    Verdu, J
    Rychly, J
    Matisova-Rychla, L
    [J]. POLYMER DEGRADATION AND STABILITY, 1997, 58 (03) : 283 - 289
  • [4] Metallocene ethylene-1-octene copolymers: Influence of comonomer content on thermo-mechanical, rheological, and thermo-oxidative behaviours before and after melt processing in an internal mixer
    Al-Malaika, S.
    Peng, X.
    Watson, H.
    [J]. POLYMER DEGRADATION AND STABILITY, 2006, 91 (12) : 3131 - 3148
  • [5] Al-Malaika S, 1993, ATMOSPHERIC OXIDATIO, V1, P45, DOI DOI 10.1016/B978-0-444-89615-5.50006-8
  • [6] THERMAL AND PHOTOCHEMICAL OXIDATION OF POLYPROPYLENE - INFLUENCE OF RESIDUAL CATALYST LEVELS IN UNSTABILIZED DILUENT AND GAS-PHASE POLYMERS
    ALLEN, NS
    FATINIKUN, KO
    HENMAN, TJ
    [J]. EUROPEAN POLYMER JOURNAL, 1983, 19 (07) : 551 - 554
  • [7] Degradation of low-density polyethylene during extrusion.: VI.: Effects of oxygen content in air gap
    Andersson, T
    Wesslén, B
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2005, 96 (05) : 1767 - 1775
  • [8] [Anonymous], 1990, OXIDATION INHIBITION
  • [9] Thermal degradation behaviour of poly(oxymethylene):: 1.: Degradation and stabilizer consumption
    Archodoulaki, VM
    Lüftl, S
    Seidler, S
    [J]. POLYMER DEGRADATION AND STABILITY, 2004, 86 (01) : 75 - 83
  • [10] ROLE OF OXYGEN DIFFUSION IN POLYMER AGING - KINETIC AND MECHANICAL ASPECTS
    AUDOUIN, L
    LANGLOIS, V
    VERDU, J
    DEBRUIJN, JCM
    [J]. JOURNAL OF MATERIALS SCIENCE, 1994, 29 (03) : 569 - 583
12345678910