Investigating creep rupture and damage behaviour in notched P92 steel specimen using a microscale modelling approach

被引：23
作者：
Zhao, L. [1 ,2 ]
Alang, N. [2 ]
Nikbin, K. [2 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300072, Peoples R China
[2] Imperial Coll London, Dept Mech Engn, London SW7 2AZ, England
来源：
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2018年 / 41卷 / 02期
基金：
中国国家自然科学基金;
关键词：
creep fracture; microscale modelling; notched specimen; strain rate dependent; Voronoi tessellation; CRACK-GROWTH RATE; STRESS; PREDICTION; DEFORMATION; FRACTURE; FAILURE; GRAIN; DUCTILITY; FATIGUE; JOINTS;
D O I：
10.1111/ffe.12713
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Idealized random grains separated by pseudo grain boundaries were generated by using Voronoi tessellation to simulate the polycrystalline microstructure. Combined with finite element analyses, this approach made it possible to addressing crack initiation and progressive failure due to crack growth in notched bar geometries of P92 steel at high temperature. The calculations provided good predictions for creep rupture lives of notched specimen with different notch radii and external stress. Simultaneously, irregular crack growth shape, intergranular crack mode, and wedge cracks at triple grain interaction were captured in the model. The crack initiation positions were found to be influenced by notch radius and applied stress causing high stress triaxiality at the subgrain level. Furthermore, the preferential crack growth directions were changed as the notch varied from sharp to blunt.
引用
收藏
页码：456 / 472
页数：17
相关论文
共 51 条
[1]   Advances on creep-fatigue damage assessment in notched components [J].
Barbera, D. ;
Chen, H. ;
Liu, Y. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (11) :1854-1867
[2]   Environmental creep intergranular damage and multisite crack evolution model for engineering alloys [J].
Biglari, F. ;
Nikbin, K. M. .
COMPUTATIONAL MATERIALS SCIENCE, 2014, 84 :267-277
[3]   A diffusion driven carburisation combined with a multiaxial continuum creep model to predict random multiple cracking in engineering alloys [J].
Biglari, F. R. ;
Nikbin, K. M. .
ENGINEERING FRACTURE MECHANICS, 2015, 146 :89-108
[4]   The effect of multiaxial stress state on creep behavior and fracture mechanism of P92 steel [J].
Chang, Yuan ;
Xu, Hong ;
Ni, Yongzhong ;
Lan, Xiang ;
Li, Hongyuan .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 636 :70-76
[5]   Effect of Notch on Creep Behavior of 316L(N) SS [J].
Charde, S. R. ;
Ballal, A. R. ;
Peshwe, D. R. ;
Mathew, M. D. ;
Paretkar, R. K. .
6TH INTERNATIONAL CONFERENCE ON CREEP, FATIGUE AND CREEP-FATIGUE INTERACTION, 2013, 55 :517-525
[6]   Microscale-calibrated modeling of the deformation response of dual-phase steels [J].
Chen, Peng ;
Ghassemi-Armaki, Hassan ;
Kumar, Sharvan ;
Bower, Allan ;
Bhat, Shrikant ;
Sadagopan, Sriram .
ACTA MATERIALIA, 2014, 65 :133-149
[7]   INTERGRANULAR FRACTURE DURING POWER-LAW CREEP UNDER MULTIAXIAL STRESSES [J].
COCKS, ACF ;
ASHBY, MF .
METAL SCIENCE, 1980, 14 (8-9) :395-402
[8]   Creep failure model of a tempered martensitic stainless steel integrating multiple deformation and damage mechanisms [J].
Gaffard, V ;
Besson, J ;
Gourgues-Lorenzon, AF .
INTERNATIONAL JOURNAL OF FRACTURE, 2005, 133 (02) :139-166
[9]   Generalized approach to estimation of strains and stresses at blunt V-notches under non-localized creep [J].
Gallo, P. ;
Berto, F. ;
Glinka, G. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (03) :292-306
[10]   Towards efficient spall generation simulation in rolling element bearing [J].
Gazizulin, D. ;
Klein, R. ;
Bortman, J. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (09) :1389-1405
123456