Magnetic and dielectric properties of Ba12Fe28Ti15O84 layered ferrite ceramics

In this study we report for the first time the magnetic and dielectric properties of the quaternary layered ferrite Ba12Fe28Ti15O84. Dense ferrite ceramics were prepared by conventional sintering using powders obtained by solid-state reaction and by coprecipitation. Only the latter powder resulted in nearly single phase ceramics, whereas larger amounts of secondary phases were observed in the material obtained by the solid-state route. According to the HRTEM investigation, the ferrite lattice is originated by the intergrowth of perovskite-like and spinel-like slabs and can be considered as a natural magnetic superlattice. A ferrimagnetic order with saturation magnetization of approximate to 12.5 A m(2) kg(-1) and coercivity of similar to 1590 A m(-1) (similar to 20 Oe) is proposed at room temperature. The thermomagnetic data indicate a Curie temperature of similar to 420 K for the quaternary ferrite. An additional magnetic transition was detected at similar to 700 K and ascribed to a secondary magnetic phase, probably the solid solution of TiO2 in BaFe12O19. An intrinsic relative dielectric constant of the order of 23-50 at room temperature was measured at 10(9) Hz. At lower frequency the dielectric behaviour is dominated by extrinsic effects related to the heterogeneous electrical nature of the ceramics corresponding to semiconducting grains separated by more insulating grain boundary regions. The dielectric losses are rather high, often >1, indicating an overall semiconducting character of the material.