Effect of shot peening on the fatigue life of a Zr-based bulk metallic glass

被引：47
|
作者：
Raghavan, R. [1 ]
Ayer, R. [2 ]
Jin, H. W. [2 ]
Marzinsky, C. N. [2 ]
Ramamurty, U. [1 ]
机构：
[1] Indian Inst Sci, Dept Mat Engn, Bangalore 560012, Karnataka, India
[2] ExxonMobil Res & Engn Co, Adv Struct Mat Sect, Annandale, NJ 08801 USA
来源：
SCRIPTA MATERIALIA | 2008年 / 59卷 / 02期
关键词：
metallic glasses; nanoindentation; fatigue; shear bands; residual stresses;
D O I：
10.1016/j.scriptamat.2008.03.009
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The fatigue lives of a Zr-based bulk metallic glass (BMG) in the as-cast and shot-peened conditions were evaluated. Results suggest that shot peening does not cause significant enhancement of the fatigue performance of the BMG. Cracks were observed to nucleate in subsurface regions. This was attributed to the domination of the compressive residual stress field on the surface over deformation-induced plastic flow softening that otherwise leads to easy nucleation of shear bands which act like microcracks. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：167 / 170
页数：4
相关论文
共 50 条
  • [21] Temperature Effect on Fracture of a Zr-Based Bulk Metallic Glass
    Yang, Na
    Yi, Jun
    Yang, Yu Hang
    Huang, Bo
    Jia, Yan Dong
    Kou, Sheng Zhong
    Wang, Gang
    MATERIALS, 2020, 13 (10)
  • [22] Effect of Inhomogeneity of Zr-based Bulk Metallic Glass Plate on Fatigue Strength under Torsion
    Nakai, Yoshikazu
    Nakagawa, Kenichi
    Mikami, Kohei
    THERMEC 2011, PTS 1-4, 2012, 706-709 : 1331 - 1336
  • [23] Experimental and Statistical Analysis of Fatigue Behavior in Zr-based Bulk Metallic Glass
    Yao, Zhifeng
    Qiao, Jichao
    Jean-Marc, Pelletier
    Yao, Yao
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (11) : 3010 - 3016
  • [24] Mechanisms and mechanics of fatigue crack propagation in Zr-based bulk metallic glass
    Department of Mechanical Engineering, Kobe University, 1-1, Rokkodai, Nada Kobe 657-8501, Japan
    不详
    Key Eng Mat, 2008, (317-328):
  • [25] Fatigue of Zr-based Bulk Metallic Glass under Cyclic-torsion
    Nakai, Y.
    Nakagawa, K.
    Mikami, K.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
  • [26] Fractography of fatigue crack propagation in a nanocrystalline Zr-based bulk metallic glass
    Fujita, K
    Inoue, A
    Zhang, A
    SCRIPTA MATERIALIA, 2001, 44 (8-9) : 1629 - 1633
  • [27] Comments on "The fatigue-endurance limit of a Zr-based bulk metallic glass"
    Wang, G. Y.
    Landes, J. D.
    Peker, A.
    Liaw, P. K.
    SCRIPTA MATERIALIA, 2007, 57 (01) : 65 - 68
  • [28] Fatigue strength of sharp notched plate of Zr-based bulk metallic glass
    Nakai, Y.
    Fujihara, K.
    Sei, N.
    Ando, K.
    Kim, B. K.
    FATIGUE 2010, 2010, 2 (01): : 147 - 154
  • [29] Response to comments on "The fatigue endurance limit of a Zr-based bulk metallic glass"
    Menzel, B. C.
    Dauskardt, R. H.
    SCRIPTA MATERIALIA, 2007, 57 (01) : 69 - 71
  • [30] Effect of laser shock peening without absorbent coating on the mechanical properties of Zr-based bulk metallic glass
    Zhu, Yunhu
    Fu, Jie
    Zheng, Chao
    Ji, Zhong
    OPTICS AND LASER TECHNOLOGY, 2015, 75 : 157 - 163
12345