Electrochemical and morphological properties of zirconium conversion coating in the presence of nickel ions on galvanized steel

被引：23
作者：
Asemani, H. R. [1 ]
Sarabi, A. A. [1 ]
Mohammadloo, H. Eivaz [1 ]
Sarayloo, M. [1 ]
机构：
[1] Amirkabir Univ Technol, Fac Polymer Engn & Color Technol, POB 15875-4413, Tehran, Iran
来源：
JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH | 2016年 / 13卷 / 05期
关键词：
Zirconium conversion coating; Nickel; EIS; Polarization; FE-SEM; X-ray; Photoelectron spectroscopy; RAY PHOTOELECTRON-SPECTROSCOPY; ELECTROGALVANIZED STEEL; CORROSION PERFORMANCE; XPS; SURFACE; BEHAVIOR; GROWTH; ALLOY; PROTECTION; RESISTANCE;
D O I：
10.1007/s11998-016-9800-x
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
A hexafluorozirconic acid-based conversion coating was applied on a galvanized steel substrate and the influence of nickel ion from nickel sulfate solution (in zirconium solution and in a separate solution) on the corrosion resistance behavior and morphology of zirconium conversion coating was investigated. Electrochemical impedance spectroscopy and DC polarization were conducted in 3.5 wt% NaCl solution in order to optimize practical conditions of zirconium conversion coating and NiSO4 solution on the galvanized steel substrate. Field emission scanning electron microscopy and X-ray photoelectron spectroscopy were employed to study the morphology and composition of the coated surfaces. Results revealed that the conversion coating obtained from solution containing zirconium and nickel ions (Zr + Ni) did not improve corrosion resistance and uniformity of the coating in comparison with Zr conversion coating in optimized condition. However, a positive effect was obtained from samples coated with separate solutions of zirconium and nickel (Zr-Ni). Improved corrosion resistance and morphology of Zr-based conversion coating were observed in Ni2+ concentration, pH, and immersion time of 10 g/L, 6 and 300 s, respectively. Morphology and surface composition analysis proved that two separate layers of conversion coating containing zirconium, zinc, and nickel oxide/hydroxide compounds were formed in the case samples that were treated by separate solutions. This led to better uniformity and higher thickness of the coating. Finally, adhesion strength of epoxy organic coating on galvanized steel with and without conversion coating was investigated by pull-off measurement. Zr-Ni conversion coating in optimum conditions had a positive effect on adhesion of organic coating in comparison with blank sample and samples pretreated with Zr and Zr + Ni conversion coatings through increased surface roughness and physical interlocking.
引用
收藏
页码：883 / 894
页数：12
相关论文
共 56 条
[1]   Hexafluorozirconic acid based surface pretreatments: Characterization and performance assessment [J].
Adhikari, Saikat ;
Unocic, K. A. ;
Zhai, Y. ;
Frankel, G. S. ;
Zimmerman, John ;
Fristad, W. .
ELECTROCHIMICA ACTA, 2011, 56 (04) :1912-1924
[2]   The effect of pH and role of Ni2+ in zinc phosphating of 2024-Al alloy.: Part I:: Macroscopic studies with XPS and SEM [J].
Akhtar, A. S. ;
Wong, K. C. ;
Mitchell, K. A. R. .
APPLIED SURFACE SCIENCE, 2006, 253 (02) :493-501
[3]   Effect of zirconium conversion coating: Adhesion and anti-corrosion properties of epoxy organic coating containing zinc aluminum polyphosphate (ZAPP) pigment on carbon mild steel [J].
Asemani, H. R. ;
Ahmadi, P. ;
Sarabi, A. A. ;
Mohammadloo, H. Eivaz .
PROGRESS IN ORGANIC COATINGS, 2016, 94 :18-27
[4]   Chemical and electrochemical considerations on the removal process of hexavalent chromium from aqueous media [J].
Barrera-Díaz, C ;
Palomar-Pardavé, M ;
Romero-Romo, M ;
Martínez, S .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 2003, 33 (01) :61-71
[5]   Anion distributions in sodium silicate solutions. Characterization by Si-29 NMR and infrared spectroscopies, and vapor phase osmometry [J].
Bass, JL ;
Turner, GL .
JOURNAL OF PHYSICAL CHEMISTRY B, 1997, 101 (50) :10638-10644
[6]   Voltammetric and XPS investigations of nickel hydroxide electrochemically dispersed on gold surface electrodes [J].
Casella, IG ;
Guascito, MR ;
Sannazzaro, MG .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1999, 462 (02) :202-210
[7]  
Cornell M., 2003, The Iron Oxides Structure, Properties, Reactions, Occurrence and Uses, Vsecond
[8]  
Da Fonte Jr B, 1982, US Patent, Patent No. [4. 359. 345, 4359345]
[9]  
Dillard JI, 1908, INORGANIC CHEM ELEME
[10]   Systematic XPS studies of metal oxides, hydroxides and peroxides [J].
Dupin, JC ;
Gonbeau, D ;
Vinatier, P ;
Levasseur, A .
PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2000, 2 (06) :1319-1324
123456