Cavitation erosion of plasma-sprayed CoMoCrSi coatings

被引：55

作者：

Wang, Yan ^{[1
]}

Liu, Jiangwei ^{[1
]}

Kang, Nan ^{[1
]}

Darut, Geoffrey ^{[1
]}

Poirier, Thierry ^{[2
]}

Stella, Jorge ^{[3
]}

Liao, Hanlin ^{[1
]}

Planche, Marie-Pierre ^{[1
]}

机构：

[1] Univ Bourgogne Franche Comte, UTBM, LERMPS, Belfort, France

[2] Inst Ceram Francaise, Limoges, France

[3] Univ Simon Bolivar, Dept Ciencia Mat, Caracas, Venezuela

来源：

TRIBOLOGY INTERNATIONAL | 2016年 / 102卷

关键词：

Cavitation erosion; CoMoCrSi coating; Plasma spraying; Surface 3D profile; BEHAVIOR; STEEL; RESISTANCE; CORROSION; WEAR;

D O I：

10.1016/j.triboint.2016.06.014

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

CoMoCrSi coatings were manufactured on a steel substrate by atmospheric plasma spraying (APS), followed by a three-hour heat treatment at a temperature of 800 degrees C and 1000 degrees C, respectively. Prior to the ultrasonic test of the cavitation erosion, coating cross-sections were observed by scanning electron microscopy (SEM) and analyzed by X-ray diffraction (XRD). 3D profiles were employed to investigate the erosion mechanism on both pristine and eroded surfaces. As a result, it is shown that the heat treatment can significantly reduce the mean erosion depth of the CoMoCrSi coatings and the cavitation damages mainly consist of the removal of the splashes with weak adhesion during plasma spray and the delamination of fragments from bubble collapses. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：429 / 435

页数：7

共 20 条

[1] On the collapse of cavities
Bourne, NK
[J]. SHOCK WAVES, 2002, 11 (06) : 447 - 455
[2] Cavitation erosion behavior of ion-nitrided 34 CrAlNi 7 steel with different microstructures
da Silva, F. J.
Marinho, R. R.
Paes, M. T. P.
Franco, S. D.
[J]. WEAR, 2013, 304 (1-2) : 183 - 190
[3] Hydro turbine failure mechanisms: An overview
Dorji, Ugyen
Ghomashchi, Reza
[J]. ENGINEERING FAILURE ANALYSIS, 2014, 44 : 136 - 147
[4] Development of a cavitation erosion model
Dular, Matevz
Stoffel, Bernd
Sirok, Brane
[J]. WEAR, 2006, 261 (5-6) : 642 - 655
[5] THE FRACTURE-BEHAVIOR OF 2 CO-MO-CR-SI WEAR RESISTANT ALLOYS (TRIBALOYS)
HALSTEAD, A
RAWLINGS, RD
[J]. JOURNAL OF MATERIALS SCIENCE, 1985, 20 (04) : 1248 - 1256
[6] Hart D., 2007, REV CAVITATION EROSI
[7] Synergistic effect of ultrasonic cavitation erosion and corrosion of WC-CoCr and FeCrSiBMn coatings prepared by HVOF spraying
Hong, Sheng
Wu, Yuping
Zhang, Jianfeng
Zheng, Yugui
Zheng, Yuan
Lin, Jinran
[J]. ULTRASONICS SONOCHEMISTRY, 2016, 31 : 563 - 569
[8] Cavitation Erosion Behavior and Mechanism of HVOF Sprayed WC-10Co-4Cr Coating in 3.5 wt% NaCl Solution
Hong, Sheng
Wu, Yuping
Zhang, Jianfeng
Zheng, Yugui
Qin, Yujiao
Gao, Wenwen
Li, Gaiye
[J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2015, 68 (01) : 151 - 159
[9] Cavitation erosion and jet impingement erosion mechanism of cold sprayed Ni-Al2O3 coating
Hu, H. X.
Jiang, S. L.
Tao, Y. S.
Xiong, T. Y.
Zheng, Y. G.
[J]. NUCLEAR ENGINEERING AND DESIGN, 2011, 241 (12) : 4929 - 4937
[10] Thermally sprayed coatings for protection of fretting wear in land-based gas-turbine engine
Koiprasert, H
Dumrongrattana, S
Niranatlumpong, P
[J]. WEAR, 2004, 257 (1-2) : 1 - 7

← 1 2 →