Dual-Templating Preparation and Enhanced Low-Temperature Reducibility of Three-Dimensionally Ordered Macroporous Ceria with Mesoporous Walls

被引：20
作者：
Zhang Han [1 ]
Zhang Lei [1 ]
Deng Jiguang [1 ]
Liu Yuxi [1 ]
Jiang Haiyan [1 ]
Shi Fengjuan [1 ]
Ji Kemeng [1 ]
Dai Hongxing [1 ]
机构：
[1] Beijing Univ Technol, Dept Chem & Chem Engn, Coll Environm & Energy Engn, Beijing 100124, Peoples R China
来源：
CHINESE JOURNAL OF CATALYSIS | 2011年 / 32卷 / 05期
关键词：
dual-templating preparation method; three-dimensionally ordered macropore; ceria; low-temperature reducibility; wormhole-like mesoporous wall; surfactant; PREFERENTIAL OXIDATION; MAGNESIUM-OXIDE; SOLID-SOLUTIONS; METAL-OXIDES; CEO2; SILICA; FABRICATION; CATALYSTS; NANORODS; GASES;
D O I：
10.1016/S1872-2067(10)60196-9
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Three-dimensionally ordered macroporous (3DOM) ceria with mesoporous walls and cubic crystal structures were prepared with polymethyl methacrylate (PMMA) as a hard template and triblock copolymer Pluronic F127 (EO(106)PO(70)EO(106)), cetyltrimethylammonium bromide (CTAB), or poly(ethylene glycol) (PEG) as a soft template. Citric acid was used as a complexing agent and cerium nitrate was used as a metal precursor. The 3DOM CeO(2) samples were characterized by numerous analytical techniques. The as-fabricated CeO(2) samples had a 3DOM architecture with polycrystalline wormhole-like mesoporous walls. The nature of the soft template had an important effect on the pore structure and the surface area of the final product. The surface areas of the F127-, CTAB-, and PEG-derived 3DOM CeO(2) samples (denoted CeO(2)-F127, CeO(2)-CTAB, and CeO(2)-PEG, respectively) were ca. 60.5, 60.2, and 51.8 m(2)/g, respectively. The low-temperature reducibility of the 3DOM-structured CeO(2) samples was much better than that of the bulk counterpart and the low-temperature reducibility of the three 3DOM ceria samples increased according to CeO(2)-PEG < CeO(2)-CTAB < CeO(2)-F127, which coincided with the surface oxygen vacancy density sequence. The improved physicochemical properties associated with the formation of the 3DOM skeleton with wormhole-like mesoporous walls may be useful for applications such as CeO(2)-materials in heterogeneous catalysis.
引用
收藏
页码：842 / 852
页数：11
相关论文
共 48 条
[41]   Promoting effect of Ti addition on three-dimensionally ordered macroporous Mn-Ce catalysts for NH3-SCR reaction: Enhanced N2 selectivity and remarkable water resistance [J].
Wang, Xiaofeng ;
Zhao, Zhe ;
Xu, Yang ;
Li, Qingbo .
APPLIED SURFACE SCIENCE, 2021, 569
[42]   One-pot synthesis of core-shell Au@CeO2-δ nanoparticles supported on three-dimensionally ordered macroporous ZrO2 with enhanced catalytic activity and stability for soot combustion [J].
Wei, Yuechang ;
Zhao, Zhen ;
Yu, Xuehua ;
Jin, Baofang ;
Liu, Jian ;
Xu, Chunming ;
Duan, Aijun ;
Jiang, Guiyuan ;
Ma, Shuhua .
CATALYSIS SCIENCE & TECHNOLOGY, 2013, 3 (11) :2958-2970
[43]   Three-dimensionally ordered macroporous Sn4+-doped TiO2 with anatase-rutile mixed phase via Pt loading by photoreduction method: enhanced photodegradation and hydrogen production performance [J].
Zhou, Qianlong ;
Li, Li ;
Xin, Yuying ;
Liu, Dongxue ;
Zhang, Xinyue .
NEW JOURNAL OF CHEMISTRY, 2018, 42 (18) :15190-15199
[44]   Facile preparation of ordered mesoporous MnCo2O4 for low-temperature selective catalytic reduction of NO with NH3 [J].
Qiu, Mingying ;
Zhan, Sihui ;
Yu, Hongbing ;
Zhu, Dandan ;
Wang, Shengqiang .
NANOSCALE, 2015, 7 (06) :2568-2577
[45]   Facile preparation of 3D ordered mesoporous CuOx-CeO2 with notably enhanced efficiency for the low temperature oxidation of heteroatom-containing volatile organic compounds [J].
He, Chi ;
Yu, Yanke ;
Chen, Changwei ;
Yue, Lin ;
Qiao, Nanli ;
Shen, Qun ;
Chen, Jinsheng ;
Hao, Zhengping .
RSC ADVANCES, 2013, 3 (42) :19639-19656
[46]   The synergistic catalytic effect between graphene oxide and three-dimensional ordered mesoporous Co3O4 nanoparticles for low-temperature CO oxidation [J].
Zhao, Yinshuang ;
Dong, Fang ;
Han, Weiliang ;
Zhao, Haijun ;
Tang, Zhicheng .
MICROPOROUS AND MESOPOROUS MATERIALS, 2019, 273 :1-9
[47]   Low-temperature catalytic steam reforming of toluene as a biomass tar model compound over three-dimensional ordered macroporous Ni-Pt/Ce1-xZrxO2 catalysts [J].
Zhou, Shuyu ;
Chen, Zezhi ;
Gong, Huijuan ;
Wang, Xiaoshu ;
Zhu, Tingting ;
Zhou, Yuchen .
APPLIED CATALYSIS A-GENERAL, 2020, 607
[48]   Enhancement of SO2 Resistance on Submonolayer V2O5-MnO2/CeO2 Catalyst by Three-Dimensional Ordered Mesoporous CeO2 in Low-Temperature NH3-SCR [J].
Ni, Kaiwen ;
Peng, Yuewang ;
Wang, Yuting ;
Huang, Zhiwei ;
Zhao, Huawang ;
Wu, Xiaomin ;
Jing, Guohua .
ENERGY & FUELS, 2022, 36 (05) :2787-2798
12345