Dual-Templating Preparation and Enhanced Low-Temperature Reducibility of Three-Dimensionally Ordered Macroporous Ceria with Mesoporous Walls

被引：19

作者：

Zhang Han ^{[1
]}

Zhang Lei ^{[1
]}

Deng Jiguang ^{[1
]}

Liu Yuxi ^{[1
]}

Jiang Haiyan ^{[1
]}

Shi Fengjuan ^{[1
]}

Ji Kemeng ^{[1
]}

Dai Hongxing ^{[1
]}

机构：

[1] Beijing Univ Technol, Dept Chem & Chem Engn, Coll Environm & Energy Engn, Beijing 100124, Peoples R China

来源：

CHINESE JOURNAL OF CATALYSIS | 2011年 / 32卷 / 05期

关键词：

dual-templating preparation method; three-dimensionally ordered macropore; ceria; low-temperature reducibility; wormhole-like mesoporous wall; surfactant; PREFERENTIAL OXIDATION; MAGNESIUM-OXIDE; SOLID-SOLUTIONS; METAL-OXIDES; CEO2; SILICA; FABRICATION; CATALYSTS; NANORODS; GASES;

D O I：

10.1016/S1872-2067(10)60196-9

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

Three-dimensionally ordered macroporous (3DOM) ceria with mesoporous walls and cubic crystal structures were prepared with polymethyl methacrylate (PMMA) as a hard template and triblock copolymer Pluronic F127 (EO(106)PO(70)EO(106)), cetyltrimethylammonium bromide (CTAB), or poly(ethylene glycol) (PEG) as a soft template. Citric acid was used as a complexing agent and cerium nitrate was used as a metal precursor. The 3DOM CeO(2) samples were characterized by numerous analytical techniques. The as-fabricated CeO(2) samples had a 3DOM architecture with polycrystalline wormhole-like mesoporous walls. The nature of the soft template had an important effect on the pore structure and the surface area of the final product. The surface areas of the F127-, CTAB-, and PEG-derived 3DOM CeO(2) samples (denoted CeO(2)-F127, CeO(2)-CTAB, and CeO(2)-PEG, respectively) were ca. 60.5, 60.2, and 51.8 m(2)/g, respectively. The low-temperature reducibility of the 3DOM-structured CeO(2) samples was much better than that of the bulk counterpart and the low-temperature reducibility of the three 3DOM ceria samples increased according to CeO(2)-PEG < CeO(2)-CTAB < CeO(2)-F127, which coincided with the surface oxygen vacancy density sequence. The improved physicochemical properties associated with the formation of the 3DOM skeleton with wormhole-like mesoporous walls may be useful for applications such as CeO(2)-materials in heterogeneous catalysis.

引用

页码：842 / 852

页数：11

共 48 条

[31] Three-dimensionally ordered macroporous K0.5MnCeOx/SiO2 catalysts: facile preparation and worthwhile catalytic performances for soot combustion [J].

Yu, Xuehua ;

Zhao, Zhen ;

Wei, Yuechang ;

Zhao, Linlin ;

Liu, Jian .

CATALYSIS SCIENCE & TECHNOLOGY, 2019, 9 (06) :1372-1386

[32] Preparation of Three-dimensionally Ordered Macroporous Spinel Li1.6Mn1.6O4 and Adsorption Characteristics of Lithium Ion-sieve [J].

Lu Hong-Yan ;

Yang Li-Xin ;

Wu Sai-Xiang ;

Zhang Ling-Jun ;

Zhou Li ;

Liu Xiao-Li .

CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2011, 32 (10) :2268-2273

[33] Alkali/alkaline-earth metal-modified MnOx supported on three-dimensionally ordered macroporous-mesoporous TixSi1-xO2 catalysts: Preparation and catalytic performance for soot combustion [J].

Peng, Chao ;

Yu, Di ;

Zhang, Chunlei ;

Chen, Maozhong ;

Wang, Lanyi ;

Yu, Xuehua ;

Fan, Xiaoqiang ;

Zhao, Zhen ;

Cheng, Kai ;

Chen, Yongsheng ;

Wei, Yuechang ;

Liu, Jian .

JOURNAL OF ENVIRONMENTAL SCIENCES, 2023, 125 :82-94

[34] Preparation of three-dimensionally ordered macroporous La0.6Sr0.4Fe0.8Bi0.2O3-δ and their excellent catalytic performance for the combustion of toluene [J].

Zhao, Zhenxuan ;

Dai, Hongxing ;

Deng, Jiguang ;

Du, Yucheng ;

Liu, Yuxi ;

Zhang, Lei .

JOURNAL OF MOLECULAR CATALYSIS A-CHEMICAL, 2013, 366 :116-125

[35] Three-Dimensionally Orientation-Controlled Ge Rods on an Insulator Formed by Low-Temperature Ni-Induced Lateral Crystallization [J].

Ishiyama, Takamitsu ;

Imajo, Toshifumi ;

Saitoh, Noriyuki ;

Yoshizawa, Noriko ;

Suemasu, Takashi ;

Toko, Kaoru .

CRYSTAL GROWTH & DESIGN, 2022, 22 (02) :1123-1129

[36] Preparation of Three-Dimensionally Ordered Macroporous Composite Bi2O3/TiO2 and Its Photocatalytic Degradation of Crystal Violet under Multiple Modes [J].

Huang Xian-Dan ;

Li Li ;

Wei Qiu-Ying ;

Zhang Wen-Zhi ;

Lu Lu .

ACTA PHYSICO-CHIMICA SINICA, 2013, 29 (12) :2615-U176

[37] Dual cocatalysts decorated three dimensionally ordered mesoporous g-C3N4 with homogeneous wall thickness for enhanced photocatalytic performance [J].

Bi, Jingce ;

Zhao, Shan ;

Wu, Junbiao ;

Xu, Yan ;

Wang, Zhuopeng ;

Han, Yide ;

Zhang, Xia .

APPLIED ORGANOMETALLIC CHEMISTRY, 2020, 34 (04)

[38] Synthesis of three-dimensionally ordered macroporous composite Ag/Bi2O3-TiO2 by dual templates and its photocatalytic activities for degradation of organic pollutants under multiple modes [J].

Li, Li ;

Huang, Xiandan ;

Hu, Tianyu ;

Wang, Jianxin ;

Zhang, Wenzhi ;

Zhang, Jianqi .

NEW JOURNAL OF CHEMISTRY, 2014, 38 (11) :5293-5302

[39] Preparation of three-dimensionally ordered macroporous MFe2O4 (M = Co, Ni, Cu) spinel catalyst and its simultaneous catalytic application in CO oxidation and NO plus CO reaction [J].

Liu, Hao ;

Liu, Liuhui ;

Wei, Longqing ;

Chu, Bingxian ;

Qin, Zuzeng ;

Jin, Guangzhou ;

Tong, Zhangfa ;

Dong, Lihui ;

Li, Bin .

FUEL, 2020, 272

[40] Gold nanoparticles supported on ceria-modified mesoporous–macroporous binary metal oxides as highly active catalysts for low-temperature water–gas shift reaction [J].

V. Idakiev ;

T. Tabakova ;

K. Tenchev ;

Z. Y. Yuan ;

T. Z. Ren ;

A. Vantomme ;

B. L. Su .

Journal of Materials Science, 2009, 44 :6637-6643

← 1 2 3 4 5 →