Dual-Templating Preparation and Enhanced Low-Temperature Reducibility of Three-Dimensionally Ordered Macroporous Ceria with Mesoporous Walls

被引：20

作者：

Zhang Han ^{[1
]}

Zhang Lei ^{[1
]}

Deng Jiguang ^{[1
]}

Liu Yuxi ^{[1
]}

Jiang Haiyan ^{[1
]}

Shi Fengjuan ^{[1
]}

Ji Kemeng ^{[1
]}

Dai Hongxing ^{[1
]}

机构：

[1] Beijing Univ Technol, Dept Chem & Chem Engn, Coll Environm & Energy Engn, Beijing 100124, Peoples R China

来源：

CHINESE JOURNAL OF CATALYSIS | 2011年 / 32卷 / 05期

关键词：

dual-templating preparation method; three-dimensionally ordered macropore; ceria; low-temperature reducibility; wormhole-like mesoporous wall; surfactant; PREFERENTIAL OXIDATION; MAGNESIUM-OXIDE; SOLID-SOLUTIONS; METAL-OXIDES; CEO2; SILICA; FABRICATION; CATALYSTS; NANORODS; GASES;

D O I：

10.1016/S1872-2067(10)60196-9

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

Three-dimensionally ordered macroporous (3DOM) ceria with mesoporous walls and cubic crystal structures were prepared with polymethyl methacrylate (PMMA) as a hard template and triblock copolymer Pluronic F127 (EO(106)PO(70)EO(106)), cetyltrimethylammonium bromide (CTAB), or poly(ethylene glycol) (PEG) as a soft template. Citric acid was used as a complexing agent and cerium nitrate was used as a metal precursor. The 3DOM CeO(2) samples were characterized by numerous analytical techniques. The as-fabricated CeO(2) samples had a 3DOM architecture with polycrystalline wormhole-like mesoporous walls. The nature of the soft template had an important effect on the pore structure and the surface area of the final product. The surface areas of the F127-, CTAB-, and PEG-derived 3DOM CeO(2) samples (denoted CeO(2)-F127, CeO(2)-CTAB, and CeO(2)-PEG, respectively) were ca. 60.5, 60.2, and 51.8 m(2)/g, respectively. The low-temperature reducibility of the 3DOM-structured CeO(2) samples was much better than that of the bulk counterpart and the low-temperature reducibility of the three 3DOM ceria samples increased according to CeO(2)-PEG < CeO(2)-CTAB < CeO(2)-F127, which coincided with the surface oxygen vacancy density sequence. The improved physicochemical properties associated with the formation of the 3DOM skeleton with wormhole-like mesoporous walls may be useful for applications such as CeO(2)-materials in heterogeneous catalysis.

引用

页码：842 / 852

页数：11

共 48 条

[21] Self-templating construction of mesopores on three-dimensionally ordered macroporous La0.5Sr0.5MnO3 perovskite with enhanced performance for soot combustion [J].

Zhao, Peng ;

Fang, Fan ;

Feng, Nengjie ;

Chen, Chong ;

Liu, Geng ;

Chen, Li ;

Zhu, Zhongjian ;

Meng, Jie ;

Wan, Hui ;

Guan, Guofeng .

CATALYSIS SCIENCE & TECHNOLOGY, 2019, 9 (08) :1835-1846

[22] Nanosized Au supported on three-dimensionally ordered mesoporous β-MnO2: Highly active catalysts for the low-temperature oxidation of carbon monoxide, benzene, and toluene [J].

Ye, Qing ;

Zhao, Jiansheng ;

Huo, Feifei ;

Wang, Dao ;

Cheng, Shuiyuan ;

Kang, Tianfang ;

Dai, Hongxing .

MICROPOROUS AND MESOPOROUS MATERIALS, 2013, 172 :20-29

[23] Synthesis of ZnO-CuO and ZnO-Co3O4 Materials with Three-Dimensionally Ordered Macroporous Structure and Its H2S Removal Performance at Low-Temperature [J].

Yu, Tao ;

Chen, Zhuo ;

Wang, Yundong ;

Xu, Jianhong .

PROCESSES, 2021, 9 (11)

[24] Preparation and Catalytic Performance of Three-Dimensionally Ordered Macroporous Perovskite-Type LaFeO3 Catalyst for Soot Combustion [J].

Xu Junfeng ;

Liu Jian ;

Zhao Zhen ;

Zhang Guizhen ;

Duan Aijun ;

Jiang Guiyuan ;

Xu Chunming .

CHINESE JOURNAL OF CATALYSIS, 2010, 31 (02) :236-241

[25] Highly dispersed MnOx nanoparticles supported on three-dimensionally ordered macroporous carbon: a novel nanocomposite for catalytic reduction of NOx with NH3 at low temperature [J].

Gao, Xin ;

Li, Ling ;

Song, Lihong ;

Lu, Ting ;

Zhao, Jiaxin ;

Liu, Zhi .

RSC ADVANCES, 2015, 5 (37) :29577-29588

[26] Preparation of K Modified Three-Dimensionally Ordered Macroporous MnCeOx/Ti0.7Si0.3O2 Catalysts and Their Catalytic Performance for Soot Combustion [J].

Zhang, Chunlei ;

Yu, Di ;

Peng, Chao ;

Wang, Lanyi ;

Fan, Xiaoqiang ;

Yu, Xuehua ;

Zhao, Zhen .

PROCESSES, 2021, 9 (07)

[27] Catalytic toluene oxidation over the three-dimensionally ordered macroporous EuFeO3 catalysts fabricated by the sucrose-assisted polymethyl methacrylate-templating method [J].

Ji, Kemeng ;

Dai, Hongxing ;

Deng, Jiguang ;

Zhang, Han ;

Zhang, Lei ;

Jiang, Haiyan .

SOLID STATE SCIENCES, 2014, 27 :36-42

[28] Glycol-assisted construction of three-dimensionally ordered macroporous ZnO-Cu2O-TiO2 with enhanced photocatalytic properties [J].

Yang, Renchun ;

Lu, Xiaojia ;

Zhang, Huan ;

Tao, Tingxian ;

Ren, Yiming ;

Li, Fang ;

Zhu, Lingting .

APPLIED SURFACE SCIENCE, 2016, 362 :237-243

[29] Three-dimensionally ordered macroporous WO3 modified Ag3PO4 with enhanced visible light photocatalytic performance [J].

Xu, Hui ;

Zhao, Haozhu ;

Xu, Yuanguo ;

Chen, Zhigang ;

Huang, Liying ;

Li, Yeping ;

Song, Yanhua ;

Zhang, Qi ;

Li, Huaming .

CERAMICS INTERNATIONAL, 2016, 42 (01) :1392-1398

[30] Creation of three-dimensionally ordered macroporous Au/CeO2 catalysts with controlled pore sizes and their enhanced catalytic performance for formaldehyde oxidation [J].

Zhang, Jun ;

Jin, Ying ;

Li, Changyan ;

Shen, Yuenian ;

Han, Li ;

Hu, Zhongxue ;

Di, Xiaowei ;

Liu, Zhiliang .

APPLIED CATALYSIS B-ENVIRONMENTAL, 2009, 91 (1-2) :11-20

← 1 2 3 4 5 →