Mechanical Properties of Porous Ti-Co Alloy for Medical Application by Gelcasting

被引：0

作者：

Yang Donghua ^{[1
]}

Shao Huiping ^{[1
]}

Guo Zhimeng ^{[1
]}

Lin Tao ^{[1
]}

Fan Lianpeng ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Adv Mat & Technol Inst, Beijing 100083, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2011年 / 40卷 / 10期

关键词：

gelcasting; porous metal; Ti-Co alloys; mechanical properties; TITANIUM IMPLANTS; FABRICATION; METAL; POROSITY;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Porous titanium based alloys containing 8 wt% and 12 wt% cobalt elements were prepared by gelcasting methods. The concentration of dispersant for obtain the stable suspension slurry were studied. The microstructure, the total porosity and the mechanical properties of the sintered porous Ti-Co alloys were investigated by scaning electronic microscopy, X-ray diffraction, compression and bending tests. The results show that 1 wt% of the optimal dispersant amount is selected, at which viscosity of the suspension slurry is low. Open and closed three-dimensional pore morphologies and total porosity around 50% can be achieved. In contrast to porous Ti by gelcasting available before, porous Ti-Co alloys present excellent properties. The compressive strength ranging from 68-378 MPa, the bending strength ranging from 53.68-169.17 MPa and Young's modulus ranging from 7-21 GPa. In this study, porous Ti-8Co alloy (33 vol%) which have great properties matching adult bone, therefore being suited for medical applications.

引用

页码：1822 / 1826

页数：5

共 12 条

[1] Bandyopadhyay A, 2009, ACTA BIOMATER, V20, P29
[2] Bandyopadhyay A, 2008, J MATER SCI-MATER M, V19, P1007
[3] Fabrication of porous NiTi shape memory alloy for hard tissue implants by combustion synthesis
Chu, CL
Chung, CY
Lin, PH
Wang, SD
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 366 (01): : 114 - 119
[4] Correlation of in vitro and in vivo results of vacuum plasma sprayed titanium implants with different surface topography
Endres, Stefan
Wilke, Monika
Knoell, Peter
Frank, Holger
Kratz, Marita
Wilke, Axel
[J]. JOURNAL OF MATERIALS SCIENCE-MATERIALS IN MEDICINE, 2008, 19 (03) : 1117 - 1125
[5] Direct metal fabrication of titanium implants with tailored materials and mechanical properties using electron beam melting technology
Harrysson, Ola L. A.
CansiZoglu, Omer
Marcellin-Little, Denis J.
Cormier, Denis R.
West, Harvey A., II
[J]. MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS, 2008, 28 (03): : 366 - 373
[6] Cellular Ti-6Al-4V structures with interconnected macro porosity for bone implants fabricated by selective electron beam melting
Heinl, Peter
Mueller, Lenka
Koerner, Carolin
Singer, Robert F.
Mueller, Frank A.
[J]. ACTA BIOMATERIALIA, 2008, 4 (05) : 1536 - 1544
[7] Low stiffness porous Ti structures for load-bearing implants
Krishna, B. Vamsi
Bose, Susmita
Bandyopadhyay, Amit
[J]. ACTA BIOMATERIALIA, 2007, 3 (06) : 997 - 1006
[8] Fabrication of fully porous and porous-surfaced Ti-6Al-4V implants by electro-discharge-sintering of spherical Ti-6Al-4V powders in an one-step process
Lee, W. H.
Hyun, C. Y.
[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 189 (1-3) : 219 - 223
[9] Li Y, 2008, POWDER METALLURGY IN, V18, P10
[10] Porosity and mechanical properties of porous titanium fabricated by gelcasting
Li Yan
Guo Zhimeng
Hao Junjie
Ren Shubin
[J]. RARE METALS, 2008, 27 (03) : 282 - 286

← 1 2 →