Thermomechanical fatigue behavior of an air plasma sprayed thermal barrier coating system

被引：12
|
作者：
Chen, Z. B. [1 ,3 ]
Wang, Z. G. [1 ]
Zhu, S. J. [2 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
[2] Fukuoka Inst Technol, Dept Intelligent Mech Engn, Higashi Ku, Fukuoka 8110295, Japan
[3] Aviation Ind Corp China, Shenyang Aeroengine Res Inst, Shenyang 110015, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2011年 / 528卷 / 29-30期
关键词：
Thermal barrier coating; Thermomechanical fatigue; Air plasma spraying; MECHANICAL FATIGUE; DAMAGE MECHANISMS; SUPERALLOY; EVOLUTION; LIFE;
D O I：
10.1016/j.msea.2011.08.031
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Failure behavior of an air plasma sprayed thermal barrier coating (TBC) system was investigated under in-phase (IP) and out-of-phase (OP) thermomechanical fatigue (TMF) tests. All the TMF tests were performed in the temperature range of 450-850 degrees C with a given period of 300s under mechanical strain control. Both the bond coat NiCrAlY and the top coat 7%Y(2)O(3)-ZrO(2) were fabricated by air plasma spraying (APS). Results revealed that the IP TMF lifetime was longer than that of the OP TMF under the same mechanical strain amplitude. Morphology observations of the failed specimens showed that the coating cracking and spallation processes were different in the two phase conditions. (C) 2011 Elsevier B.V. All rights reserved.
引用
收藏
页码：8396 / 8401
页数：6
相关论文
共 50 条
  • [1] Effect of thermal Gradient on the Thermomechanical Fatigue Behavior of Thermal Barrier Coating System
    Huang, Feng
    Zhou, Zhong-Jiao
    Hua, Xu
    Chen, Guo-Feng
    Zhou, Xiao-Zhou
    PROCEEDINGS OF THE 4TH 2016 INTERNATIONAL CONFERENCE ON MATERIAL SCIENCE AND ENGINEERING (ICMSE 2016), 2016, 101 : 328 - 333
  • [2] Thermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
    Lu, Zhe
    Myoung, Sang-Won
    Jung, Yeon-Gil
    Balakrishnan, Govindasamy
    Lee, Jeongseung
    Paik, Ungyu
    MATERIALS, 2013, 6 (08) : 3387 - 3403
  • [3] Thermomechanical behavior of plasma-sprayed zirconia thermal barrier coatings
    Singh, JP
    Sutaria, M
    Chopra, A
    22ND ANNUAL CONFERENCE ON COMPOSITES, ADVANCED CERAMICS, MATERIALS, AND STRUCTURES: B, 1998, 19 (04): : 313 - 321
  • [4] The surface cracking behavior in air plasma sprayed thermal barrier coating system incorporating interface roughness effect
    Zhang, W. X.
    Fan, X. L.
    Wang, T. J.
    APPLIED SURFACE SCIENCE, 2011, 258 (02) : 811 - 817
  • [5] Thermal fatigue damage behavior of plasma sprayed thermal barrier coatings
    Yamazaki, Yasuhiro
    Yoshida, Toshihiko
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VIII, 2010, 417-418 : 85 - 88
  • [6] Tensile damage evolution behavior in plasma-sprayed thermal barrier coating system
    Qian, LH
    Zhu, SJ
    Kagawa, Y
    Kubo, T
    SURFACE & COATINGS TECHNOLOGY, 2003, 173 (2-3): : 178 - 184
  • [7] Thermomechanical Evaluation and Thermal Expansion Behavior of Plasma-sprayed Thermal Barrier Coatings
    Takagi, Kenta
    Kawasaki, Akira
    Harada, Yoshio
    Okazaki, Masakazu
    MULTISCALE, MULTIFUNCTIONAL AND FUNCTIONALLY GRADED MATERIALS, 2010, 631-632 : 85 - +
  • [8] Constrained sintering of an air-plasma-sprayed thermal barrier coating
    Cocks, A. C. F.
    Fleck, N. A.
    ACTA MATERIALIA, 2010, 58 (12) : 4233 - 4244
  • [9] Microstructure of air plasma sprayed YSZ nanostructured thermal barrier coating
    Zhang, YJ
    Sun, XF
    Jin, T
    Zhao, NR
    Guan, HG
    Hu, ZQ
    ACTA METALLURGICA SINICA, 2003, 39 (04) : 395 - 398
  • [10] Measurements and understanding of the stiffness of an air plasma sprayed thermal barrier coating
    Chen, Ying
    Li, Chun
    Zhao, Xiaofeng
    Xiao, Ping
    SURFACE & COATINGS TECHNOLOGY, 2020, 394
12345