Composite materials based on wastes of flat glass processing

被引：29

作者：

Gorokhovsky, AV

Escalante-Garcia, JI

Gashnikova, GY

Nikulina, LP

Artemenko, SE

机构：

[1] CINVESTAV, Unidad Saltillo, Dept Ceram Engn, Saltillo 25000, Coahuila, Mexico

[2] Saratov State Tech Univ, Inst Technol, Dept Chem Technol, Engels 413100, Russia

来源：

WASTE MANAGEMENT | 2005年 / 25卷 / 07期

关键词：

D O I：

10.1016/j.wasman.2004.11.007

中图分类号：

X [环境科学、安全科学];

学科分类号：

08 ; 0830 ;

摘要：

Glass mirrors scrap and poly (vinyl) butiral waste (PVB) obtained from flat glass processing plants we're investigated as raw materials to produce composites, The emphasis was on studying the influence of milled glass-mirror waste contents on properties of composites-produced with PVB. The characterization involved: elongation under rupture, water absorption, tensile strength and elastic modulus tests. The results showed. that the composite containing 10 wt% of filler powder had the best properties among the compositions studied. The influence of the time of exposure in humid atmosphere on the composite properties was investigated. It was found that the admixture of PVB iso-propanol solution to the scrap of glass mirrors during milling provided stabilization of the properties of the composites produced. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：733 / 736

页数：4

共 12 条

[1] DHALIWAL AK, 2000, THERMOCHIM ACTA, V391, P245
[2] FOSS RV, 1997, P 6 INT C ARCH AUT G, P44
[3] Garner J, 1996, GLASS TECHNOL, V37, P151
[4] Polyvinyl butyral based solid polymeric electrolytes: Preliminary studies
Gopal, S
Ramchandran, R
Agnihotry, RSA
[J]. SOLAR ENERGY MATERIALS AND SOLAR CELLS, 1997, 45 (01) : 17 - 25
[5] Volume fraction effects on interfacial adhesion strength of glass-fiber-reinforced polymer composites
Gu, W
Hu, HF
Kampe, SL
Lu, GQ
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 277 (1-2): : 237 - 243
[6] PHYSICAL-CHEMISTRY OF GLASS SURFACES
HENCH, LL
CLARK, DE
[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 1978, 28 (01) : 83 - 105
[7] The effect of particle-matrix adhesion on the mechanical behavior of glass filled epoxies. Part 2. A study on fracture toughness
Kawaguchi, T
Pearson, RA
[J]. POLYMER, 2003, 44 (15) : 4239 - 4247
[8] KELLER U, 1999, P 6 INT C ARCH AUT G, P353
[9] Wide web coating of complex materials
Lievens, H
[J]. SURFACE & COATINGS TECHNOLOGY, 1995, 76-77 (1-3) : 744 - 753
[10] Effect of substrate preconditioning on charge transport at the phthalocyanine-conducting polymer film interface
Radhakrishnan, S
Unde, S
[J]. THIN SOLID FILMS, 1999, 347 (1-2) : 229 - 232

← 1 2 →