Yttrium sol-gel coating effects on the cyclic oxidation behaviour of 304 stainless steel

被引：31
作者：
Riffard, F
Buscail, H
Caudron, E
Cueff, R
Issartel, C
Perrier, S
机构：
来源：
CORROSION SCIENCE | 2003年 / 45卷 / 12期
关键词：
stainless steel; yttrium; sol-gel coating; high temperature oxidation; in situ X-ray diffraction;
D O I：
10.1016/S0010-938X(03)00114-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The present results reveal the interest of sol-gel coating technique to improve 304 steel high temperature oxidation resistance. An yttrium sol-gel coating appears to enhance the oxidation resistance during isothermal oxidation test, to decrease widely the oxide weight gain and to reduce the initial transient oxidation stage generally observed in the case of blank steels. Moreover, the experimental results confirm that yttrium sol-gel coating also plays a significant role on the cyclic oxidation behaviour of the 304 steel. In fact, the yttrium addition promotes remarkably the prolongation of the period during which the oxide scale still remains adherent to the substrate. (C) 2003 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2867 / 2880
页数：14
相关论文
共 61 条
[1]   OXIDATION BEHAVIOR OF COCRAL SYSTEMS CONTAINING ACTIVE ELEMENT ADDITIONS [J].
ALLAM, IM ;
WHITTLE, DP ;
STRINGER, J .
OXIDATION OF METALS, 1978, 12 (01) :35-66
[2]   IMPROVEMENTS IN OXIDATION RESISTANCE BY DISPERSED OXIDE ADDITION - AL2O3-FORMING ALLOYS [J].
ALLAM, IM ;
WHITTLE, DP ;
STRINGER, J .
OXIDATION OF METALS, 1979, 13 (04) :381-401
[3]  
Antoni L, 1999, EUR FED CORR PUBL, P187
[4]  
ARMANET F, 1990, ACIERS INOXYDABLES
[5]   EFFECT OF ALLOY GRAIN-SIZE AND SILICON CONTENT ON THE OXIDATION OF AUSTENITIC FE-CR-NI-MN-SI ALLOYS IN PURE O2 [J].
BASU, SN ;
YUREK, GJ .
OXIDATION OF METALS, 1991, 36 (3-4) :281-315
[6]   THE INFLUENCE OF CERIUM, YTTRIUM AND LANTHANUM ION-IMPLANTATION ON THE OXIDATION BEHAVIOR OF A 20CR-25NI-NB STAINLESS-STEEL IN CARBON-DIOXIDE AT 900-1050-DEGREES-C [J].
BENNETT, MJ ;
BISHOP, HE ;
CHALKER, PR ;
TUSON, AT .
MATERIALS SCIENCE AND ENGINEERING, 1987, 90 :177-190
[7]  
BENNETT MJ, 1989, ROLE ACTIVE ELEMENTS, P11
[8]   Initial stages of oxidation of yttrium-implanted pure iron and various steels at 700°C under low oxygen partial pressure [J].
Caudron, E ;
Buscail, H .
CORROSION SCIENCE, 2001, 43 (08) :1477-1495
[9]   In-situ X-ray diffraction study of the behaviour of yttrium implanted low manganese-carbon steel at high temperature [J].
Caudron, E ;
Buscail, H ;
Cueff, R .
SURFACE & COATINGS TECHNOLOGY, 2000, 126 (2-3) :266-271
[10]   Study of the initial stages of oxidation of yttrium-implanted chromium using X-ray diffraction and absorption spectroscopy [J].
Cristobal, MJ ;
Gibson, PN ;
Stroosnijder, MF .
CORROSION SCIENCE, 1996, 38 (06) :805-822
1234567