Preparation and Electrocatalytic Performance for Hydrogen Evolution Reaction of the Ni/LaNi5 Porous Composite Electrode

被引:0
作者
Zhang Yi [1 ]
Wang Senlin [1 ]
Li Caicai [1 ]
机构
[1] Huaqiao Univ, Dept Appl Chem, Coll Mat Sci & Engn, Xiamen 361021, Peoples R China
关键词
Ni/LaNi5; porous composite electrode; hydrogen evolution reaction; stability; CATHODES; BEHAVIOR;
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
At first, the Ni-Zn coating was electroplated, then, the coating was immersed in concentrated alkali solution to remove zinc and the porous nickel was obtained. Finally, the Ni/LaNi5 porous composite electrode was prepared on this porous nickel surface by means of the composite electro-deposition. The electro-catalytic properties for hydrogen evolution reaction of the electrode were evaluated by electrochemical steady-state polarization curve and electrochemical impendence spectroscopy (EIS). And the stability of the electrode was studied by open circuit potential and constant potential electrolysis technology for long time and discontinuity electrolysis. Results show that the apparent exchange current density of the porous composite electrode is 172 and 26 times as much as that of the nickel electrode and the porous nickel electrode, respectively. Because LaNi5 possesses the effect of electrode protection, the stability of the porous composite electrode is better than that of the porous nickel.
引用
收藏
页码:457 / 461
页数:5
相关论文
共 25 条
[1]  
Ba Qiang, 2007, SHIP SCI TECHNOLOGY, P6
[2]  
[宋全生 Song Quansheng], 2005, [天津大学学报. 自然科学与工程技术版, Journal of Tianjin University.], V38, P508
[3]   STATE OF OVERPOTENTIAL-DEPOSITED H-SPECIES AT ELECTROPLATED PLATINUM SURFACES IN COMPARISON WITH BRIGHT PLATINUM [J].
ELAM, M ;
CONWAY, BE .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 1987, 17 (05) :1002-1020
[4]  
Fan Shaohua, 1998, J WUHAN U, V44, P703
[5]   COMPARISON AND EVALUATION OF ELECTROCATALYTIC MATERIALS IN ELECTROCHEMICAL HYDROGEN-PRODUCTION [J].
FIORI, G ;
MARI, CM .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1987, 12 (03) :159-164
[6]  
Flores N., 2005, J MOL CATAL A-CHEM, V226, P179
[7]   PROGRESS ON THE DEVELOPMENT OF ACTIVATED CATHODES FOR WATER ELECTROLYSIS [J].
GIZ, MJ ;
SILVA, JCP ;
FERREIRA, M ;
MACHADO, SAS ;
TICIANELLI, EA ;
AVACA, LA ;
GONZALEZ, ER .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1992, 17 (09) :725-729
[8]   HYDROGEN EVOLUTION REACTION ON NI-S ELECTRODES IN ALKALINE-SOLUTIONS [J].
GONZALEZ, ER ;
AVACA, LA ;
TREMILIOSI-FILHO, G ;
MACHADO, SAS ;
FERREIRA, M .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1994, 19 (01) :17-21
[9]  
Han Q, 2008, ACTA METALL SIN, V44, P887
[10]   Electrocatalytic properties of new electrocatalysts for hydrogen evolution in alkaline water electrolysis [J].
Hu, WK .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2000, 25 (02) :111-118