Nanoneedles of Lanthanum Oxide (La2O3): A Novel Functional Material for Microwave Absorber Material

被引:9
|
作者
Adi, W. A. [1 ]
Wardiyati, S. [1 ]
Dewi, S. H. [1 ]
机构
[1] BATAN, Ctr Sci & Technol Adv Mat, Kawasan Puspiptek Serpon, Indonesia
来源
4TH INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS SCIENCE AND TECHNOLOGY, 2016 | 2017年 / 202卷
关键词
Lanthanum oxide; nanoneedle; rare earth; microwave absorber; NANOSTRUCTURES;
D O I
10.1088/1757-899X/202/1/012066
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Lanthanum oxideSynthesis and characterization of La2O3 nanoneedles have been successfully carried out by using hydrolysis reaction with NH4OH as a solvent. La2O3 was prepared from LaCl3 solution. LaCl3 was preheated on a hotplate and stirred by using a magnetic stirrer, then added solution of NH4OH 1 M with the variation speed drops of 3 ml, 6 ml and 9 ml to obtain white precipitation La(OH)(3) until a pH of 9. Stirring was continued until 1 hour. A white precipitate formed is separated from the effluent by centrifugation method with 3000 rpm and neutral pH. Then, the precipitate was dried in an oven at a temperature of 70 degrees C and sintered at 1000 degrees C to get La2O3 nanoneedles. The identification of sample phase was carried out by using X-ray diffractometer (XRD). The refinement results of X-ray diffraction pattern shows that the samples have a single phase of La2O3. The morphology of the nanoneedles was observed by using the transmission electron microscope (TEM). Meanwhile, the reflection and transmission of electromagnetic wave were measured by using the vector network analyzer (VNA) at X-band frequency.
引用
收藏
页数:8
相关论文
共 50 条
  • [41] A NEW FORM OF LA2O3
    FELSCHE, J
    NATURWISSENSCHAFTEN, 1969, 56 (04) : 212 - &
  • [42] CO sensing properties of novel nanostructured La2O3 microspheres
    Michel, Carlos R.
    Martinez-Preciado, Alma H.
    SENSORS AND ACTUATORS B-CHEMICAL, 2015, 208 : 355 - 362
  • [43] A study on the synthesis of lanthanum oxide (La2O3) from NaLa(SO4)(2)center dot H2O by metathesis reaction
    Kim, Dae-Weon
    Ahn, Nak-Kyoon
    Shim, Hyun-Woo
    Lee, Chan-Gi
    Choi, Hee-Lack
    Hong, Hyun Seon
    JOURNAL OF THE KOREAN CRYSTAL GROWTH AND CRYSTAL TECHNOLOGY, 2018, 28 (05): : 211 - 216
  • [44] A novel nanocomposite Mo-4%La2O3 cathode
    Wang, XG
    Song, H
    Wang, ML
    Ding, BJ
    MATERIALS LETTERS, 2005, 59 (14-15) : 1756 - 1759
  • [45] NO reduction with H2 or CO over La2O3 and Sr-promoted La2O3
    Huang, SJ
    Walters, AB
    Vannice, MA
    JOURNAL OF CATALYSIS, 1998, 173 (01) : 229 - 237
  • [46] Sol-solvothermal synthesis and microwave evolution of La(OH)3 nanorods to La2O3 nanorods
    Tang, B
    Ge, JC
    Wu, CJ
    Zhuo, LH
    Niu, JY
    Chen, ZZ
    Shi, ZQ
    Dong, YB
    NANOTECHNOLOGY, 2004, 15 (09) : 1273 - 1276
  • [47] Effect of La2O3 addition on microstructure and microwave dielectric properties of Al2O3 ceramics
    Qian, Fenling
    Xie, Zhipeng
    Sun, Jialin
    Wang, Feng
    Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2012, 40 (12): : 1708 - 1712
  • [48] Effect of La2O3 on the viscosity and structure of CaO-SiO2(-Al2O3)-La2O3 melts
    Guo, Wentao
    Ding, Ziqi
    Wang, Jinming
    Wu, Jun
    Wang, Zhi
    MATERIALS CHEMISTRY AND PHYSICS, 2021, 266
  • [49] Characterization of La2O3/SiO2 mixed oxide catalyst supports
    Vidal, H
    Bernal, S
    Baker, RT
    Finol, D
    Omil, JAP
    Pintado, JM
    Rodríguez-Izquierdo, JM
    JOURNAL OF CATALYSIS, 1999, 183 (01) : 53 - 62
  • [50] The adsorption and reaction of NO, CH4 and O2 on La2O3 and Sr-promoted La2O3
    Huang, SJ
    Walters, AB
    Vannice, MA
    APPLIED CATALYSIS B-ENVIRONMENTAL, 1998, 17 (03) : 183 - 193