Nanoneedles of Lanthanum Oxide (La2O3): A Novel Functional Material for Microwave Absorber Material

被引:9
|
作者
Adi, W. A. [1 ]
Wardiyati, S. [1 ]
Dewi, S. H. [1 ]
机构
[1] BATAN, Ctr Sci & Technol Adv Mat, Kawasan Puspiptek Serpon, Indonesia
来源
4TH INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS SCIENCE AND TECHNOLOGY, 2016 | 2017年 / 202卷
关键词
Lanthanum oxide; nanoneedle; rare earth; microwave absorber; NANOSTRUCTURES;
D O I
10.1088/1757-899X/202/1/012066
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Lanthanum oxideSynthesis and characterization of La2O3 nanoneedles have been successfully carried out by using hydrolysis reaction with NH4OH as a solvent. La2O3 was prepared from LaCl3 solution. LaCl3 was preheated on a hotplate and stirred by using a magnetic stirrer, then added solution of NH4OH 1 M with the variation speed drops of 3 ml, 6 ml and 9 ml to obtain white precipitation La(OH)(3) until a pH of 9. Stirring was continued until 1 hour. A white precipitate formed is separated from the effluent by centrifugation method with 3000 rpm and neutral pH. Then, the precipitate was dried in an oven at a temperature of 70 degrees C and sintered at 1000 degrees C to get La2O3 nanoneedles. The identification of sample phase was carried out by using X-ray diffractometer (XRD). The refinement results of X-ray diffraction pattern shows that the samples have a single phase of La2O3. The morphology of the nanoneedles was observed by using the transmission electron microscope (TEM). Meanwhile, the reflection and transmission of electromagnetic wave were measured by using the vector network analyzer (VNA) at X-band frequency.
引用
收藏
页数:8
相关论文
共 50 条
  • [21] Preparation of La(OH)3 and La2O3 with rod morphology by simple hydration of La2O3
    Ding Jiawen
    Wu Yanli
    Sun Weili
    Li Yongxiu
    JOURNAL OF RARE EARTHS, 2006, 24 (04) : 440 - 442
  • [22] Ionization energies and structures of small lanthanum oxide clusters (La2O3)n.LaO (n = 1–3)
    Soumen Bhattacharyya
    Prasenjit Sen
    Sheo Mukund
    Suresh Yarlagadda
    Debashis Bandyopadhyay
    Sanjay G. Nakhate
    The European Physical Journal D, 2019, 73
  • [23] Preparation of La(OH)3 and La2O3 with Rod Morphology by Simple Hydration of La2O3
    丁家文
    吴燕利
    孙伟丽
    李永绣
    Journal of Rare Earths, 2006, (04) : 440 - 442
  • [24] Fe3O4/MWCNT/TiO2 nanocomposites as excellent microwave absorber material
    Qoidah, Siti Nikmatul
    Subadra, ST. Ulfawanti Intan
    Taufiq, Ahmad
    Mufti, Nandang
    Sunaryono, Sunaryono
    Hidayat, Nurul
    Handoko, Erfan
    Alaydrus, Mudrik
    Amrillah, Tahta
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 970
  • [25] Optical and radiation shielding properties for novel glass material: TeO2/Nb2O5/Ta2O5/La2O3
    Hussein, K., I
    Alqahtani, F. F.
    Alqahtani, M. S.
    Alzahrani, K. J.
    Zahran, H. Y.
    Alshehri, A. M.
    Yahia, I. S.
    Reben, M.
    Alqahtani, A. M.
    Yousef, E.
    CHALCOGENIDE LETTERS, 2022, 19 (06): : 417 - 427
  • [26] Morphology and Vibrational Modes of Lanthanum Oxide (La2O3) Nanoparticles Prepared with Reflux Routes at Different Reaction Times
    S. Karthikeyan
    M. Parthibavarman
    Mustafa K. A. Mohammed
    Safa H. Mohammed
    M. Selvapandiyan
    V. T. Srisuvetha
    Chemistry Africa, 2022, 5 : 1427 - 1432
  • [27] Morphology and Vibrational Modes of Lanthanum Oxide (La2O3) Nanoparticles Prepared with Reflux Routes at Different Reaction Times
    Karthikeyan, S.
    Parthibavarman, M.
    Mohammed, Mustafa K. A.
    Mohammed, Safa H.
    Selvapandiyan, M.
    Srisuvetha, V. T.
    CHEMISTRY AFRICA-A JOURNAL OF THE TUNISIAN CHEMICAL SOCIETY, 2022, 5 (05): : 1427 - 1432
  • [28] Microporous carbon with highly dispersed nano-lanthanum oxide (La2O3) for enhanced adsorption of methylene blue
    Achari, V. Sivanandan
    Lopez, Raichel Mary
    Rajalakshmi, A. S.
    Jayasree, S.
    Shibin, O. M.
    John, Deepthi
    Sekkar, V
    SEPARATION AND PURIFICATION TECHNOLOGY, 2021, 279
  • [29] Surface segregation of La2O3 molecules in Mo La2O3 cathode materials
    王金淑
    周美玲
    聂祚仁
    张久兴
    左铁镛
    王亦曼
    TransactionsofNonferrousMetalsSocietyofChina, 2000, (06) : 745 - 748
  • [30] PREPARATION OF STOICHIOMETRIC AND OFF-STOICHIOMETRY LANTHANUM SESQUISULFIDES FROM LA2O3
    BEAUDRY, BJ
    SEUNTJENS, J
    NAKAHARA, JF
    GSCHNEIDNER, KA
    JOURNAL OF THE LESS-COMMON METALS, 1987, 127 : 266 - 266