Tribological properties of calcium fluoride-based solid lubricant coatings at high temperatures

被引：12
|
作者：
Pauleau, Y
Juliet, P
Gras, R
机构：
[1] CEA, CEREM, DEM, SGM, F-38054 Grenoble 9, France
[2] Inst Natl Polytech Grenoble, ENSEEG, F-38042 Grenoble, France
[3] Inst Super Mat & Construction Mecan, F-93407 St Ouen, France
来源：
THIN SOLID FILMS | 1998年 / 317卷 / 1-2期
关键词：
thin films; sputtering; alacrite;
D O I：
10.1016/S0040-6090(97)00569-5
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Silver, calcium fluoride (CaFx with x = 1.85) and chromium-carbon (Cr3C2) thin films have been deposited on various tribological test specimens by sputtering. The friction properties of sputter-deposited Ag and CaFx single layers as well as Ag/CaFx multilayer films were determined by ball-on-disk tribological tests conducted in room air under various experimental conditions. The tribological properties (friction coefficient and wear rate) of sputter-deposited CaFx films were also determined at 500 degrees C by pin-on-disk tribological tests performed with pin specimens made of cobalt-based alloy (alacrite). Chromium-carbon films sputter-deposited on alacrite disk and counterfaces were found to be of interest to reduce the formation of alacrite wear debris in the wear tracks whereby reduced friction coefficient and wear rate values were obtained. The friction behavior of sputter-deposited CaFx/Cr3C2 thin bilayer structures was also investigated by plane-on-plane tribological tests conducted in room air at 500 degrees C and 700 degrees C. (C) 1998 Elsevier Science S.A.
引用
收藏
页码：481 / 485
页数：5
相关论文
共 50 条
  • [21] Tribological properties of low friction coatings and thin films at high temperatures.
    Pauleau, Y
    REVUE GENERALE DE THERMIQUE, 1997, 36 (03): : 192 - 208
  • [22] Tribological Properties of Laser Microtextured Surface Bonded With Composite Solid Lubricant at High Temperature
    Hua, Xijun
    Sun, Jianguo
    Zhang, Peiyun
    Liu, Kai
    Wang, Rong
    Ji, Jinghu
    Fu, Yonghong
    JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2016, 138 (03):
  • [23] STUDY ON LEAD MONOXIDE AS SOLID LUBRICANT FOR HIGH TEMPERATURES .2. COATING PROCEDURE OF LEAD MONOXIDE AND LUBRICATING PROPERTIES OF COATINGS
    MIYAKAWA, Y
    NISHIMUR.M
    ABE, W
    JOURNAL OF JAPAN SOCIETY OF LUBRICATION ENGINEERS, 1970, 15 (08): : 469 - &
  • [24] TRIBOLOGICAL COMPOSITION OPTIMIZATION OF CHROMIUM-CARBIDE-BASED SOLID LUBRICANT COATINGS FOR FOIL GAS-BEARINGS AT TEMPERATURES TO 650-DEGREES-C
    DELLACORTE, C
    SURFACE & COATINGS TECHNOLOGY, 1988, 36 (1-2): : 87 - 97
  • [25] Superior tribological properties of powder materials with solid lubricant nanoparticles
    Rapoport, L
    Leshchinsky, V
    Lvovsky, M
    Lapsker, I
    Volovik, Y
    Feldman, Y
    Popovitz-Biro, R
    Tenne, R
    WEAR, 2003, 255 : 794 - 800
  • [26] Tribological properties and developments of tungsten disulfide solid lubricant films
    School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004, China
    Dongbei Daxue Xuebao/Journal of Northeastern University, 2008, 29 (SUPPL.): : 61 - 64
  • [27] Tribological Properties of the Solid Lubricant Layers Formed by Laser Cladding
    Katoh, Takahiro
    JOURNAL OF JAPANESE SOCIETY OF TRIBOLOGISTS, 2011, 56 (10) : 603 - 608
  • [28] Tribological properties of solid lubricant contained soft metal coating
    Usami, H.
    Yamazaki, R.
    Honda, T.
    Mihara, Y.
    PROCEEDINGS OF ASIA INTERNATIONAL CONFERENCE ON TRIBOLOGY 2018 (ASIATRIB 2018), 2018, : 359 - 360
  • [29] The influence of solid lubricant for improving tribological properties in turning process
    Reddy, N. Suresh Kumar
    Nouari, Mohammed
    LUBRICATION SCIENCE, 2011, 23 (02) : 49 - 59
  • [30] Polarization independent silicon on calcium fluoride-based MIR optical modulator
    Abd-Elkader, Ahmed El-Sayed
    Younis, B. M.
    Hameed, Mohamed Farhat O.
    Obayya, Salah S. A.
    OPTICAL AND QUANTUM ELECTRONICS, 2023, 55 (04)
12345