Effects of sliding speed on the tribological behavior of AA 7075 petroleum casing in simulated drilling environment

This work investigated the effects of sliding speed on tribological behavior of AA 7075 petroleum casing in simulated drilling environment by pin-on-disc wear test. The main wear mechanism of AA 7075 disc at low sliding speed (0.0628 m/s and 0.157 m/s) was abrasive wear and oxidative wear at middle sliding speed (0.314 m/s). As sliding speed increases to higher sliding speed (0.471 m/s and 0.628 m/s), adhesive delamination wear dominated the wear process. The tribo oxides layer can efficiently protected the alloy substrate only at sliding speed of 0.314 m/s. At higher sliding speeds, tribo oxides layer were removed quickly once it was formed due to its internal fractures of tribo oxides and lower bonging strength with substrate.