Die degradation effect on aging rate in accelerated cycling tests of SiC power MOSFET modules

被引：22
|
作者：
Luo, Haoze [1 ]
Baker, Nick [1 ]
Iannuzzo, Francesco [1 ]
Blaabjerg, Frede [1 ]
机构：
[1] Aalborg Univ, Dept Energy Technol, Aalborg, Denmark
来源：
MICROELECTRONICS RELIABILITY | 2017年 / 76卷
关键词：
THRESHOLD-VOLTAGE INSTABILITY; RELIABILITY; ISSUES;
D O I：
10.1016/j.microrel.2017.07.004
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
In order to distinguish the die and bond wire degradations, in this paper both the die and bond wire resistances of SiC MOSFET modules are measured and tested during the accelerated cycling tests. It is proved that, since the die degradation under specific conditions increases the temperature swing, bond wires undergo harsher thermomechanical stress than expected. The experimental results confirm the die-related thermal failure mechanism. An improved degradation model is proposed for the bond-wire resistance increase in case of die degradation. (C) 2017 Elsevier Ltd. All rights reserved.
引用
收藏
页码：415 / 419
页数：5
相关论文
共 50 条
  • [1] Role of Threshold Voltage Shift in Highly Accelerated Power Cycling Tests for SiC MOSFET Modules
    Luo, Haoze
    Iannuzzo, Francesco
    Turnaturi, Marcello
    IEEE JOURNAL OF EMERGING AND SELECTED TOPICS IN POWER ELECTRONICS, 2020, 8 (02) : 1657 - 1667
  • [2] Aging Precursors and Degradation Effects of SiC-MOSFET Modules Under Highly Accelerated Power Cycling Conditions
    Luo, Haoze
    Iannuzzo, Francesco
    Blaabjerg, Frede
    Turnaturi, Marcello
    Mattiuzzo, Emilio
    2017 IEEE ENERGY CONVERSION CONGRESS AND EXPOSITION (ECCE), 2017, : 2506 - 2511
  • [3] On-line solder layer degradation measurement for SiC-MOSFET modules under accelerated power cycling conditionn
    Luo, Haoze
    Reigosa, Paula Diaz
    Iannuzzo, Francesco
    Blaabjerg, Frede
    MICROELECTRONICS RELIABILITY, 2018, 88-90 : 563 - 567
  • [4] Investigation on Effects of Thermal Stress on SiC MOSFET Degradation through Power Cycling Tests
    Chen, Anjun
    Jiang, Xi
    Li, Zongjian
    Yu, Hengyu
    Wang, Jun
    Shen, Z. John
    2020 THIRTY-FIFTH ANNUAL IEEE APPLIED POWER ELECTRONICS CONFERENCE AND EXPOSITION (APEC 2020), 2020, : 1106 - 1110
  • [5] Implications of Short-Circuit Degradation on the Aging Process in Accelerated Cycling Tests of SiC MOSFETs
    Du, He
    Baker, Nick
    Iannuzzo, Francesco
    PROCEEDINGS OF THE 2020 32ND INTERNATIONAL SYMPOSIUM ON POWER SEMICONDUCTOR DEVICES AND ICS (ISPSD 2020), 2020, : 202 - 205
  • [6] Power cycling issues and challenges of SiC-MOSFET power modules in high temperature conditions
    Ibrahim, A.
    Ousten, J. P.
    Lallemand, R.
    Khatir, Z.
    MICROELECTRONICS RELIABILITY, 2016, 58 : 204 - 210
  • [7] Reliable design of SiC MOSFET power modules: experimental characterization for aging prediction
    Fukunaga, Shuhei
    Castellazzi, Alberto
    Funaki, Tsuyoshi
    2022 INTERNATIONAL POWER ELECTRONICS CONFERENCE (IPEC-HIMEJI 2022- ECCE ASIA), 2022, : 151 - 156
  • [8] Design of Aging Test System for SiC MOSFET Modules
    Shen, Chaoyue
    Wang, Fei
    Wang, Zhenye
    Ye, Zhong
    2021 IEEE WORKSHOP ON WIDE BANDGAP POWER DEVICES AND APPLICATIONS IN ASIA (WIPDA ASIA 2021), 2021, : 68 - 73
  • [9] Study of Current Density Influence on Bond Wire Degradation Rate in SiC MOSFET Modules
    Luo, Haoze
    Iannuzzo, Francesco
    Baker, Nick
    Blaabjerg, Frede
    Li, Wuhua
    He, Xiangning
    IEEE JOURNAL OF EMERGING AND SELECTED TOPICS IN POWER ELECTRONICS, 2020, 8 (02) : 1622 - 1632
  • [10] Implications of short-circuit events on power cycling of 1.2-kV/20-A SiC MOSFET power modules
    Du, H.
    Ceccarelli, L.
    Iannuzzo, F.
    Reigosa, P. D.
    MICROELECTRONICS RELIABILITY, 2019, 100
12345