Oxidation behaviour of a Ge-modified silicide coating on an Nb-Si based alloy in the moderate temperature range

被引：32
|
作者：
Wang, Changliang [1 ]
Shao, Wei [1 ,2 ]
Wang, Wan [1 ]
Zhou, Chungen [1 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Dept Mat Sci & Engn, Beijing 100191, Peoples R China
[2] Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
来源：
CORROSION SCIENCE | 2020年 / 163卷
基金：
国家重点研发计划; 中国国家自然科学基金;
关键词：
Intermetallics; Oxidation; Selective oxidation; MECHANICAL-PROPERTIES; TI; CR; AL; MICROSTRUCTURE; RESISTANCE; MO; HF; COMPOSITES; DEPOSITION;
D O I：
10.1016/j.corsci.2019.108249
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The oxidation characteristics of Ge-modified silicide coating on the Nb-Si based alloy within the moderate temperatures were investigated. Results show that the mass gains of the coated alloys are 0.41, 0.58 and 0.37 mg/cm(2) after oxidation at 700 degrees C, 750 degrees C and 800 degrees C for 100 h. There is no pest phenomenon at the test temperatures. The oxide scale is composed of amorphous aluminosilica and SiO2-GeO2 with TiO2 dispersed in some of SiO2-GeO2. The good oxidation resistance of the Ge-modified silicide coating at moderate temperatures is attributed to the selective oxidation of Ti and Si, as well as the formation of glassy SiO2-GeO2.
引用
收藏
页数：8
相关论文
共 50 条
  • [31] A novel Zr-Y modified silicide coating on Nb-Si based alloys as protection against oxidation and hot corrosion
    He, Jiahua
    Guo, Xiping
    Qiao, Yanqiang
    Luo, Fa
    CORROSION SCIENCE, 2020, 177
  • [32] Characterization of microstructure and oxidation behavior of Al modified MoSi2 coating on Nb-Si based alloy
    Jiang, Hao
    Qiao, Yanqiang
    Zhang, Weiping
    Guo, Xiping
    SURFACES AND INTERFACES, 2024, 51
  • [33] Microstructure and oxidation behavior of Mo-Si-Al coating on Nb-based alloy
    Liu, Yu
    Shao, Wei
    Wang, Changliang
    Zhou, Chungen
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 735 : 2247 - 2255
  • [34] Preparation and Oxidation Resistance of Mo-Si-B Coating on Nb-Si Based Alloy Surface
    Pang Jie
    Zhou Chun-gen
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2018, 46 (02): : 73 - 77
  • [35] Effects of B on the Microstructure and Oxidation Resistance of Nb-Ti-Si-based Ultrahigh-temperature Alloy
    Wang Jun
    Guo Xiping
    Guo Jinming
    CHINESE JOURNAL OF AERONAUTICS, 2009, 22 (05) : 544 - 550
  • [36] Co-deposition of Si and B to form oxidation-resistant coatings on an Nb-Ti-Si based ultrahigh temperature alloy by pack cementation technique
    Qiao, Yanqiang
    Shen, Zhe
    Guo, Xiping
    CORROSION SCIENCE, 2015, 93 : 126 - 137
  • [37] FORMATION OF Ge-Y MODIFIED SILICIDE COATINGS ON Nb-Ti-Si BASE ULTRAHIGH TEMPERATURE ALLOY
    Yang Lingxiao
    Guo Xiping
    Qiao Yanqiang
    Pan Ruobing
    ACTA METALLURGICA SINICA, 2013, 49 (11) : 1433 - 1438
  • [38] A novel composite Si-Mo-Ti coating with Ti concentration gradient for Nb-Si based ultrahigh temperature alloy prepared by slurry sintering
    Li, Longfei
    Guo, Xiping
    Qiao, Yanqiang
    CORROSION SCIENCE, 2023, 225
  • [39] Flow softening behavior during hot compression of a Nb-Si based ultrahigh temperature alloy
    Tang, Ye
    Guo, Xiping
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 731 : 985 - 994
  • [40] Oxidation and hot corrosion behaviors of Nb-Si based ultrahigh temperature alloys at 900 °C
    He, Jia-hua
    Guo, Xi-ping
    Qiao, Yan-qiang
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2021, 31 (01) : 207 - 221
12345