Different roles of reversed austenite, athermal martensite and tempered martensite on low-temperature toughness in ultra-low carbon medium Mn steel

被引:7
|
作者
Zhang, Danqi [1 ]
Liu, Gang [2 ]
Sun, Xinjun [2 ]
机构
[1] NCS Testing Technol Co Ltd, Beijing 100081, Peoples R China
[2] Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China
关键词
Phase transformation; Toughness; Athermal martensite; Reversed austenite; Grain boundary wetting transition; INTERCRITICAL ANNEALING PROCESS; MECHANICAL-PROPERTIES; RETAINED AUSTENITE; DEFORMATION; STABILITY; STRENGTH;
D O I
10.1016/j.matlet.2021.129958
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The -40 degrees C impact energy of 0.02C-7Mn steel strongly depended on the grain boundary (GB) wetting transition. No a/a GBs were wetted when the tempering temperature (TT) was blow Ac1, but Mn segregation embrittled the GBs resulting in the intergranular fracture mode. Ductile fracture mode was formed by transformation induced plasticity (TRIP) effect of RA after tempered between 580 degrees C and 650 degrees C, where RA was the dominant second solid phase. As the dominant second solid phases, athermal a-martensite and athermal e-martensite damaged toughness to some extent after tempered at 675 degrees C and 700 degrees C. The portion of completely wetting a/a GBs reached about 80% at 700 degrees C, and athermal a-martensite had lower toughness loss than that was induced by athermal e-martensite at 675 degrees C. (c) 2021 Elsevier B.V. All rights reserved.
引用
收藏
页数:4
相关论文
共 50 条
  • [21] Study of low-temperature redistribution of carbon interstitials in martensite
    Dabrowski, L
    Neov, S
    JOURNAL OF MATERIALS SCIENCE, 1998, 33 (16) : 4261 - 4263
  • [22] Study of low-temperature redistribution of carbon interstitials in martensite
    L. Dabrowski
    S. Neov
    Journal of Materials Science, 1998, 33 : 4261 - 4263
  • [23] Microstructure Evolution during Reverse Transformation of Austenite from Tempered Martensite in Low Alloy Steel
    Shinozaki, Tomoya
    Tomota, Yo
    Fukino, Tatsuya
    Suzuki, Tetsuya
    ISIJ INTERNATIONAL, 2017, 57 (03) : 533 - 539
  • [24] Towards accurate prediction for ultra-low carbon tempered martensite property through the cross-correlated substructures
    Jia, Xingqi
    Li, Wei
    Lu, Qi
    Zhang, Kuan
    Du, Hao
    Xu, Yuantao
    Jin, Xuejun
    MATERIALS & DESIGN, 2021, 211
  • [25] LOW-TEMPERATURE TOUGHNESS OF WATER-COOLED AND TEMPERED LOW-CARBON MANGANESE STEEL
    TANAKA, JI
    TANI, S
    OUCHI, C
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1975, 15 (01) : 19 - 26
  • [26] MORPHOLOGY AND CRYSTALLOGRAPHY OF BLOCKS AND SUB-BLOCKS IN ULTRA-LOW CARBON LATH MARTENSITE STEEL
    Morito, S.
    Edamatsu, Y.
    Adachi, Y.
    Ohba, T.
    NANOSTRUCTURED METALS: FUNDAMENTALS TO APPLICATIONS, 2009, : 261 - +
  • [27] Conditions for Grain Boundary Bulging during Tempering of Lath Martensite in Ultra-low Carbon Steel
    Tsuchiyama, Toshihiro
    Natori, Masahide
    Nakada, Nobuo
    Takaki, Setsuo
    ISIJ INTERNATIONAL, 2010, 50 (05) : 771 - 773
  • [28] MARTENSITE FORMATION AND THE RELATED TOUGHNESS IN 304-STAINLESS STEEL DURING LOW-TEMPERATURE FATIGUE
    OSHIDA, Y
    DEGUCHI, A
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1987, 10 (05) : 363 - 372
  • [29] Effect of Mn Content on Hydrogen Embrittlement Resistance of Tempered Martensite in Low Alloy Steel
    Yoshida S.
    Arai Y.
    Omura T.
    Cho K.
    Yasuda H.Y.
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 2024, 110 (04): : 385 - 394
  • [30] EFFECT OF Mn, Cr, and Ni ADDITIONS ON THE STRUCTURE, STRENGTH, AND TOUGHNESS OF TEMPERED MARTENSITE AND BAINITE IN LOW CARBON STEELS.
    Kamada, Akio
    Koshizuka, Noriaki
    Funakoshi, Tokushi
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1975, 61 (13): : 2839 - 2851