Effects of secondary orientation and temperature on the fretting fatigue behaviors of Ni-based single crystal superalloys

被引：33
|
作者：
Su, Yue [1 ]
Han, Qi-Nan [2 ]
Zhang, Cheng-Cheng [3 ]
Shi, Hui-Ji [1 ]
Niu, Li-Sha [1 ]
Deng, Guo-Jian [3 ]
Rui, Shao-Shi [1 ]
机构：
[1] Tsinghua Univ, AML, Sch Aerosp Engn, Beijing 100084, Peoples R China
[2] Aircraft Strength Res Inst China, Xian 710065, Shaanxi, Peoples R China
[3] Aero Engine Grp Corp China, Shanghai Engn Res Ctr Commercial Aircraft Engine, Commercial Aircraft Engine Co Ltd, Shanghai 200241, Peoples R China
来源：
TRIBOLOGY INTERNATIONAL | 2019年 / 130卷
基金：
中国国家自然科学基金;
关键词：
Fretting fatigue; Ni-based single crystal superalloys; Secondary orientation; Temperature effect; PLASTICITY FINITE-ELEMENT; SITU SEM OBSERVATION; CRITICAL-PLANE; CYCLE FATIGUE; CRACK INITIATION; LIFE PREDICTION; DOVETAIL JOINT; NICKEL; SIMULATION; DEFORMATION;
D O I：
10.1016/j.triboint.2018.09.006
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A dovetail fixture for fretting fatigue test was designed. Fretting fatigue experiments were performed for Nibased single crystal (NBSX) superalloys at 600 and 700 degrees C in two secondary orientations, [110] and [010]. The influence of secondary orientation and temperature on fretting fatigue behavior was investigated. The crystal plasticity finite element (CPFE) simulation was used to study the stress field at the contact region. The result indicates that the stress distribution is correlated to fretting damage, which is consistent with the crack initiation site. Fretting fatigue life is predicted based on critical plane method, which is in good agreement with the experimental result.
引用
收藏
页码：9 / 18
页数：10
相关论文
共 50 条
  • [31] Elevated temperature, high cycle fatigue behavior of carbon-containing single crystal Ni-Based superalloys
    Al-Jarba, K. A.
    Fuchs, G. E.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 760 : 287 - 295
  • [32] Fretting fatigue damage mechanism of Nickel-based single crystal superalloys at high temperature
    Sun, Shouyi
    Li, Lei
    He, Kun
    Yue, Zhufeng
    Yang, Weizhu
    Yu, Zhiyuan
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2020, 186
  • [33] Alloying effects of refractory elements in the dislocation of Ni-based single crystal superalloys
    Shiyu Ma
    Jianxin Zhang
    ProgressinNaturalScience:MaterialsInternational, 2016, 26 (06) : 636 - 642
  • [34] Alloying effects of refractory elements in the dislocation of Ni-based single crystal superalloys
    Ma, Shiyu
    Zhang, Jianxin
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2016, 26 (06) : 636 - 642
  • [35] Crack initiation mechanisms during very high cycle fatigue of Ni-based single crystal superalloys at high temperature
    Cervellon, A.
    Hemery, S.
    Kuernsteiner, P.
    Gault, B.
    Kontis, P.
    Cormier, J.
    ACTA MATERIALIA, 2020, 188 (188) : 131 - 144
  • [36] Investigations on the thermo-mechanical fatigue of two Ni-based single-crystal superalloys
    Zhou, H
    Harada, H
    Ro, Y
    Okada, I
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 394 (1-2): : 161 - 167
  • [37] Low Cycle Fatigue Failure Analysis of a Ni-Based Single Crystal Superalloys at 850 °C
    Zhang, Xuhui
    Gao, Hangshan
    Wen, Zhixun
    Zhang, Haocheng
    Yue, Zhufeng
    ADVANCED ENGINEERING MATERIALS, 2019, 21 (02)
  • [38] A comparative study of thermo-mechanical fatigue of two Ni-based single crystal superalloys
    Zhou, H
    Osawa, M
    Harda, H
    Yokokawa, T
    Koizumi, Y
    Kobayashi, I
    Waki, M
    Ro, Y
    Okada, I
    SUPERALLOYS 2004, 2004, : 225 - 231
  • [39] A review of composition evolution in Ni-based single crystal superalloys
    Wanshun Xia
    Xinbao Zhao
    Liang Yue
    Ze Zhang
    Journal of Materials Science & Technology, 2020, 44 (09) : 76 - 95
  • [40] Characterization and formation of σ/γ interface in Ni-based single crystal superalloys
    Ma, Shiyu
    Zhang, Jianxin
    Li, Xueqiao
    Mao, Shengcheng
    MATERIALS RESEARCH EXPRESS, 2017, 4 (11):
12345