Influence of TiO2 film on photo-catalytic property of enamels

被引：8

作者：

Jiang, Weizhong ^{[1
]}

Wang, Ying ^{[1
]}

Gu, Lixia ^{[1
]}

机构：

[1] Donghua Univ, Coll Mat Sci & Engn, Shanghai 200051, Peoples R China

来源：

JOURNAL OF NON-CRYSTALLINE SOLIDS | 2007年 / 353卷 / 44-46期

关键词：

photocatalysis; nanocrystals; X-ray diffraction; films and coatings; scanning electron microscopy; sol-gels(xerogels);

D O I：

10.1016/j.jnoncrysol.2007.06.072

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Ti(OC4H9)(4)-C2H5OH-H2O was used as matrix solution of titanium dioxide (TiO2) film. Through sol-gel process, enamels were coated with TiO2 film. Using methyl-orange as the simulative pollutant solution of photo-catalytic efficiency, we studied photo-catalytic activities of the enamels with and without TiO2 film. Crystal structure and microstructure of the TiO2 film were analyzed by means of scanning electron microscope (SEM) and X-ray diffract meter (XRD). Results showed that the photo-catalytic efficiency was greatly improved by the TiO2 film coated on the enamel,surface, and crystal of the TiO2 film was anatase with imperfect crystal structure at the baking temperature of 450 degrees C. The TiO2 film Consisted of a lot of very small particles (0.01-0.05 mu m and/or 10-50 nano), those particles had very small size and very large surface dimension as well as very high chemical activity, which made TiO2 film have excellent photo-catalytic degradation. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：4191 / 4194

页数：4

共 17 条

[1] The influence of solution matrix on the photocatalytic removal of color from natural waters
Bekbölet, M
Boyacioglu, Z
Özkaraova, B
[J]. WATER SCIENCE AND TECHNOLOGY, 1998, 38 (06) : 155 - 162
[2] Elina P, 2004, ENVIRON CHEM LETT, V10, P1007
[3] ELECTROCHEMICAL PHOTOLYSIS OF WATER AT A SEMICONDUCTOR ELECTRODE
FUJISHIMA, A
HONDA, K
[J]. NATURE, 1972, 238 (5358) : 37 - +
[4] Gao Lian, 2002, PHOTO CATALYTIC MAT, P158
[5] HAFFMAN MR, 1995, CHEM REV, V1, P69
[6] HARIZANOV O, 2000, ENERGY MAT SOL CELLS, V63, P177
[7] Sol-gel and CVD-metal oxide coatings for solar energy utilization
Harizanov, OA
Gesheva, KA
Stefchev, PL
[J]. CERAMICS INTERNATIONAL, 1996, 22 (02) : 91 - 94
[8] Influence of the superfine crystal of Li2Ni8O10 as mill addition on the enamel adherence
Jiang, WZ
Ying, W
Qi, D
[J]. MATERIALS LETTERS, 2004, 58 (10) : 1611 - 1615
[9] [姜勇 Jiang Yong], 2004, [材料科学与工程学报, Journal Materials Science and Engineering], V22, P584
[10] Lisebigler L, 1995, AM CHEM SOC, V95, P725

← 1 2 →