Tailored Fully Lamellar Microstructure of a Newly Developed Mn-Containing β-Solidifying γ-TiAl Alloys Rolled Bar

被引:12
作者
Li, Xiaobing [1 ]
Qian, Kun [1 ]
Shu, Lei [1 ]
Zhang, Mengshu [1 ]
Chen, Bo [1 ]
Liu, Kui [1 ,2 ]
机构
[1] Ji Hua Lab, 28 Isl Ring South Rd,Guicheng St, Foshan 528200, Guangdong, Peoples R China
[2] Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China
基金
中国国家自然科学基金;
关键词
PHASE-TRANSFORMATION BEHAVIOR; MECHANICAL-PROPERTIES; DESIGN; WORKABILITY; TECHNOLOGY; CAST;
D O I
10.1007/s11837-022-05262-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A low-cost Mn-containing beta-solidifying gamma-TiAl alloys Ti-44Al-4Mn-0.8Mo-0.1B-0.1C (at.%) alloy (named as TMM alloy) was invented. Rolled bars with a diameter of 12 mm were fabricated by conventional hot rolling, which was carried out directly from the ingot without the pre-forging and near-isothermal canned conditions. The microstructure and mechanical properties of as-rolled and heat-treated alloy bars were investigated. The rolled microstructure consists of a small amount of alpha(2)/gamma lamellar structure, while plenty of fine-grained gamma and beta(o) phases at colony boundaries. The tensile properties at room temperature were obviously improved after hot rolling by refined microstructure. At 800 degrees C, the plastic elongation can reach as high as 80.0% but with 452 MPa tensile strength due to the high amount of gamma and beta(o) phase at colony boundaries. The fully lamellar microstructure can be tailored via two-step heat treatment including solution and aging treatments. At 800 degrees C, the tensile strength, elongation, and reduction of the area were 709 MPa, 4.5%, and 7%, respectively, which was much higher than the available wrought TiAl alloys. This study serves as a completely new low-cost beta-solidifying gamma-TiAl alloy which can be continuously hot-rolled under conventional conditions.
引用
收藏
页码:2985 / 2995
页数:11
相关论文
共 26 条
[1]   The use of cast Ti-48Al-2Cr-2Nb in jet engines [J].
Bartolotta, P ;
Barrett, J ;
Kelly, T ;
Smashey, R .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1997, 49 (05) :48-&
[2]  
Chen G, 2016, NAT MATER, V15, P876, DOI [10.1038/NMAT4677, 10.1038/nmat4677]
[3]   Design, Processing, Microstructure, Properties, and Applications of Advanced Intermetallic TiAl Alloys [J].
Clemens, Helmut ;
Mayer, Svea .
ADVANCED ENGINEERING MATERIALS, 2013, 15 (04) :191-215
[4]   Thermal stability of a fully lamellar Ti-48Al-2Cr-2Nb-1B alloy [J].
Hu, D ;
Godfrey, AB ;
Loretto, MH .
INTERMETALLICS, 1998, 6 (05) :413-417
[5]   Tailoring microstructure and chemical composition of advanced γ-TiAl based alloys for improved creep resistance [J].
Kastenhuber, Michael ;
Klein, Thomas ;
Clemens, Helmut ;
Mayer, Svea .
INTERMETALLICS, 2018, 97 :27-33
[6]   Advances in Gammalloy Materials-Processes-Application Technology: Successes, Dilemmas, and Future [J].
Kim, Young-Won ;
Kim, Sang-Lan .
JOM, 2018, 70 (04) :553-560
[7]   Fracture and R-curve behavior of an intermetallic β-stabilized TiAl alloy with different nearly lamellar microstructures [J].
Leitner, T. ;
Schloffer, M. ;
Mayer, S. ;
Esslinger, J. ;
Clemens, H. ;
Pippan, R. .
INTERMETALLICS, 2014, 53 :1-9
[8]   Microstructural stability, phase evolution and mechanical properties of a forged W-modified high-Mn β-γ-TiAl alloy [J].
Li, Xiaobing ;
Tang, Hongjian ;
Xing, Weiwei ;
Zhao, Pengxiang ;
Chen, Bo ;
Ma, Yingche ;
Liu, Kui .
INTERMETALLICS, 2021, 136
[9]   Textures of rectangular extrusions and their effects on the mechanical properties of thermo-mechanically treated, lamellar microstructure, Ti-47Al-2Cr-2Nb-0.15B [J].
Liu, Renci ;
Liu, Dong ;
Tan, Jun ;
Cui, Yuyou ;
Yang, Rui ;
Liu, Feiyang ;
Withey, Paul A. .
INTERMETALLICS, 2014, 52 :110-123
[10]   Intermetallic β-Solidifying γ-TiAl Based Alloys - From Fundamental Research to Application [J].
Mayer, Svea ;
Erdely, Petra ;
Fischer, Franz Dieter ;
Holec, David ;
Kastenhuber, Michael ;
Klein, Thomas ;
Clemens, Helmut .
ADVANCED ENGINEERING MATERIALS, 2017, 19 (04)