Effect of type, form, and dosage of activators on strength of alkali-activated natural pozzolans

被引：202

作者：

Bondar, Dali ^{[1
]}

Lynsdale, C. J. ^{[2
]}

Milestone, Neil B. ^{[3
]}

Hassani, N. ^{[1
]}

Ramezanianpour, A. A. ^{[4
]}

机构：

[1] PWUT, Res Ctr Nat Disaster Ind, Tehran, Iran

[2] Univ Sheffield, Dept Civil & Struct Engn, Sheffield S1 3JD, S Yorkshire, England

[3] Univ Sheffield, Dept Mat Engn, Sheffield S1 3JD, S Yorkshire, England

[4] Amir Kabir Univ, Dept Civil Engn, Tehran, Iran

来源：

CEMENT & CONCRETE COMPOSITES | 2011年 / 33卷 / 02期

关键词：

Alkali-activated cement; Natural pozzolan; Geopolymeric cement; Activator;

D O I：

10.1016/j.cemconcomp.2010.10.021

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

It is possible to synthesize environmentally friendly cementitious construction materials from alkali-activated natural pozzolans. The effect of the alkaline medium on the strength of alkali-activated natural pozzolans has been investigated and characterised. This paper highlights the effect of the type and form of the alkaline activator, the dosage of alkali and the SiO(2)/Na(2)O ratio (silica modulus, Ms) when using water-glass solutions and different curing conditions on the geopolymerisation of natural pozzolans. Activation of natural and calcined pozzolan for production of geopolymeric binder was verified by using Taftan andesite and Shahindej dacite from Iran as a solid precursor. The optimum range for each factor is suggested based on the different effects they have on compressive strength. The concentration of dissolving silicon, aluminium and calcium in alkaline solution, the formation of gel phase and the factors affecting this have been studied by using leaching tests, ICP-AES, and FTIR. Crown Copyright (C) 2010 Published by Elsevier Ltd. All rights reserved.

引用

页码：251 / 260

页数：10

共 15 条

[1]

[Anonymous], 2009, THESIS U SHEFFIELD U

[2]

BONDAR D, 1989, P INT C SUST CONSTR, P313

[3]

Davidovits J, 1999, P GEOP INT C FR 99

[4]

Davidovits J., 1994, Journal Material Education, V16, P91, DOI DOI 10.1016/J.CEMCONCOMP.2009.12.002