Photoluminescence and Raman scattering of electrochemically deposited CdS films

被引：7

作者：

Shirai, K ^{[1
]}

Goto, F ^{[1
]}

Ichimura, M ^{[1
]}

机构：

[1] NAGOYA INST TECHNOL, CTR COOPERAT RES, NAGOYA, AICHI 466, JAPAN

来源：

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS | 1996年 / 35卷 / 11B期

关键词：

photoluminescence; Raman scattering; CdS; annealing; electrochemical deposition;

D O I：

10.1143/JJAP.35.L1483

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

CdS films were electrochemically deposited from acidic solutions containing CdSO4 and Na2S2O3. Photoluminescence spectra of these films were measured using the 325 nm Line of a He-Cd laser as the light source at 77K. For the films annealed at 300 degrees C, we observed overlapping peaks at 488 and 502 nm. The peak at 488 nm was assigned to the band-edge emission of CdS. The peak at 502 nm was thought to be due to point defects generated by annealing. bs the annealing temperature was raised, the band-edge emission became weaker and the luminescence due to the point defects shifted to longer wavelengths. These results were compared with the results of Raman scattering.

引用

页码：L1483 / L1485

页数：3

共 15 条

[1] CRYSTAL-STRUCTURE, LUMINESCENCE, AND PHOTOELECTROCHEMISTRY OF THIN ELECTROPLATED CD-CHALCOGENIDE LAYERS [J].

ABRAMOVICH, M ;

BRASIL, MJP ;

DECKER, F ;

MORO, JR ;

MOTISUKE, P ;

MULLERST, N ;

SALVADOR, P .

JOURNAL OF SOLID STATE CHEMISTRY, 1985, 59 (01) :1-8

[2] THE STRUCTURAL CHARACTERIZATION OF CADMIUM-SULFIDE FILMS GROWN BY CATHODIC ELECTRODEPOSITION [J].

BARANSKI, AS ;

FAWCETT, WR ;

MCDONALD, AC ;

DENOBRIGA, RM ;

MACDONALD, JR .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1981, 128 (05) :963-968

[3] ELECTROCHEMICAL DEPOSITION OF CDS THIN-FILMS ON MO AND AL SUBSTRATES [J].

FATAS, E ;

DUO, R ;

HERRASTI, P ;

ARJONA, F ;

GARCIACAMARERO, E .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1984, 131 (10) :2243-2246

[4] RAMAN-SPECTRA OF CUBIC ZN1-XCDXS [J].

ICHIMURA, M ;

USAMI, A ;

WADA, T ;

FUNATO, M ;

ICHINO, K ;

FUJITA, S ;

FUJITA, S .

PHYSICAL REVIEW B, 1992, 46 (07) :4273-4276

[5] TRENDS AND PROBLEMS IN CDS/CUXS THIN-FILM SOLAR-CELLS - A REVIEW [J].

MARTINUZZI, S .

SOLAR CELLS, 1982, 5 (03) :243-268

[6] ELECTROLUMINESCENCE OF POLYCRYSTALLINE CDSE THIN-FILM PHOTOELECTRODES - A SENSITIVE PROBE FOR SURFACE RECOMBINATION [J].

MULLER, N ;

ABRAMOVICH, M ;

DECKER, F ;

IIKAWA, F ;

MOTISUKE, P .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1984, 131 (09) :2204-2205

[7] EVALUATION OF ELECTRON TRAPPING PARAMETERS FROM CONDUCTIVITY GLOW CURVES IN CADMIUM SULPHIDE [J].

NICHOLAS, KH ;

WOODS, J .

BRITISH JOURNAL OF APPLIED PHYSICS, 1964, 15 (07) :783-&

[8] CHARACTERIZATION OF ELECTRON TRAPS IN CU2S-CDS POLYCRYSTALLINE CELLS BY CAPACITANCE TRANSIENT MEASUREMENTS [J].

OUALID, J ;

SARTI, D ;

GERVAIS, J ;

MARTINUZZI, S .

JOURNAL OF PHYSICS C-SOLID STATE PHYSICS, 1979, 12 (12) :2313-2321

[9] THE CATHODIC FORMATION OF PHOTOACTIVE CADMIUM-SULFIDE FILMS FROM THIOSULFATE SOLUTIONS [J].

POWER, GP ;

PEGGS, DR ;

PARKER, AJ .

ELECTROCHIMICA ACTA, 1981, 26 (05) :681-682

[10]

SHEINKMA.MK, 1969, FIZ TVERD TELA+, V10, P2069

← 1 2 →