The effect of vinyl acetate content and polyisobutylene concentration on the properties of metallocene polyethylene-ethyl vinyl acetate coextruded film for stretch and cling film applications

被引：5

作者：

McNally, GM ^{[1
]}

Small, CM ^{[1
]}

Murphy, WR ^{[1
]}

Garrett, G ^{[1
]}

机构：

[1] Queens Univ Belfast, Polymer Proc Res Ctr, Belfast BT9 5AH, Antrim, North Ireland

来源：

JOURNAL OF PLASTIC FILM & SHEETING | 2005年 / 21卷 / 01期

关键词：

polyisobutylene; LLDPE; mLLDPE; octene; EVA; cast film; coextrusion; crystallinity; tensile properties; modulus; tear strength; peel strength; tack strength; DSC; stretch; cling;

D O I：

10.1177/8756087905053791

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A range of EVA-mLLDPE-EVA coextruded films, with polyisobutylene (PIB) masterbatch content of 0-20% and vinyl acetate (VA) comonomer content of 6, 12, and 18%, is manufactured. The films are aged at 45 degrees C for up to 28 days to enable tack (cling) development. The results show that film tack strength improves significantly with aging. Increased VA concentration in the surface layer also shows significant improvement in film tack strength. The film tensile strength, elongation, and tear properties in both machine direction (MD) and transverse direction (TD) are not significantly affected by increase in PIB concentration. Increased VA content shows slight improvement in MD mechanical performance of the films, although TD properties are relatively unaffected.

引用

页码：69 / 83

页数：15

共 5 条

[1] Study of transport of small molecules through ethylene-co-vinyl acetate copolymers films.: Part A:: Water molecules [J].

Devallencourt, C ;

Marais, S ;

Saiter, JM ;

Labbé, M ;

Métayer, M .

POLYMER TESTING, 2002, 21 (03) :253-262

[2]

Lipsitt B., 1998, MED PLASTICS BIO SEP

[3] Study of transport of small molecules through ethylene-co-vinyl acetate copolymers films.: Part B:: CO2 and O2 gases [J].

Marais, S ;

Saiter, JM ;

Davallencourt, C ;

Nguyen, QT ;

Métayer, M .

POLYMER TESTING, 2002, 21 (04) :425-431

[4] The effect of extrusion processing conditions and polyisobutylene concentration on the properties of polyethylene for stretch and cling film applications [J].

Small, CM ;

McNally, GM ;

Marks, A ;

Murphy, WR .

JOURNAL OF PLASTIC FILM & SHEETING, 2002, 18 (04) :245-258

[5]

SMALL CM, 2002, ANTEC P, P2882

← 1 →