Mechanical properties of underwater friction stir welded 2219 aluminum alloy

被引：119

作者：

Liu Hui-jie ^{[1
]}

Zhang Hui-jie ^{[1
]}

Huang Yong-xian ^{[1
]}

Yu Lei ^{[1
]}

机构：

[1] Harbin Inst Technol, State Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2010年 / 20卷 / 08期

关键词：

aluminum alloy; underwater friction stir welding; mechanical property; MICROSTRUCTURE; PRECIPITATION;

D O I：

10.1016/S1003-6326(09)60309-5

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Underwater friction stir welding of 2219 aluminum alloy was carried out in order to further improve the joint performances by varying welding temperature history. The results indicated that the tensile strength of the joint can be improved from 324 MPa by external water cooling action in normal to 341 MPa. However, the plasticity of the joint is deteriorated. The underwater joint tends to fracture at the interface between the weld nugget zone and the thermal mechanically affected zone on the advancing side during tensile test, which is significantly different from the normal joint.

引用

页码：1387 / 1391

页数：5

共 17 条

[1]

[Anonymous], 2001, WELD J, V80, P30

[2] Microstructure-microhardness relationships in friction stir welded AA5251 [J].

Attallah, Moataz M. ;

Davis, Claire L. ;

Strangwood, Martin .

JOURNAL OF MATERIALS SCIENCE, 2007, 42 (17) :7299-7306

[3] Friction stir welding characteristics of different heat-treated-state 2219 aluminum alloy plates [J].

Chen, YC ;

Liu, HJ ;

Feng, JC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 420 (1-2) :21-25

[4]

Fratini L., 2008, INT J MACH TOOL MANU, V10, P42

[5] Precipitation microstructures in an AA6056 aluminium alloy after friction stir welding: Characterisation and modelling [J].

Gallais, C. ;

Denquin, A. ;

Brechet, Y. ;

Lapasset, G. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 496 (1-2) :77-89

[6] Quantitative investigation of precipitation and mechanical behaviour for AA2024 friction stir welds [J].

Genevois, C ;

Deschamps, A ;

Denquin, A ;

Doisneau-cottignies, B .

ACTA MATERIALIA, 2005, 53 (08) :2447-2458

[7]

Johnsen MR, 1999, WELD J, V78, P35

[8] Tensile properties and fracture locations of friction-stir-welded joints of 2017-T351 aluminum alloy [J].

Liu, HJ ;

Fujii, H ;

Maeda, M ;

Nogi, K .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 142 (03) :692-696

[9] Complex minimax programming under generalized type-I functions [J].

Mishra, SK .

COMPUTERS & MATHEMATICS WITH APPLICATIONS, 2005, 50 (1-2) :1-11

[10]

PAN Q, 2007, WELDING DEFECTS MECH

← 1 2 →