Carbonation and Corrosion Problems in Reinforced Concrete Structures

Reinforced concrete (RC) has been commonly used as a construction material for decades due to its high compressive strength and moderate tensile strength. However, these two properties of RC are frequently hampered by degradation. The main degradation processes in RC structures are carbonation and the corrosion of rebars. The scientific community is divided regarding the process by which carbonation causes structural damage. Some researchers suggest that carbonation weakens a structure and makes it prone to rebar corrosion, while others suggest that carbonation does not damage structures enough to cause rebar corrosion. This paper is a review of the research work carried out by different researchers on the carbonation and corrosion of RC structures. The process of carbonation and the factors that contribute to this process will be discussed, alongside recommendations for improving structures to decrease the carbonation process. The corrosion of rebars, damage to passive layers, volume expansion due to steel oxidation, and crack growth will also be discussed. Available protection methods for reducing carbonation, such as rebar structure coating, cathodic protection, and modifier implementation, will also be reviewed. The paper concludes by describing the most significant types of damage caused by carbonation, testing protocols, and mitigation against corrosion damage.