Viscosity and Liquidus Temperature of Ternary Glasses Close to the Eutectic Composition in the CaO-Al2O3-SiO2 System

被引：9
作者：
Veit, Ulrike [1 ]
Ruessel, Christian [1 ]
Houet, Yves [2 ]
Laurent, Dimitri [2 ]
机构：
[1] Univ Jena, Otto Schott Inst, Fraunhoferstr 6, D-07743 Jena, Germany
[2] 3B Fibreglass Co, S&T Ctr, Rue Charneux 59, B-4651 Battice, Belgium
来源：
INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE | 2016年 / 7卷 / 03期
关键词：
liquidus; phase transition; calcium aluminum silicate; glass forming; systems; viscosity; glass forming melts; PHYSICAL-PROPERTIES; FORMING MELTS; SILICATE; DENSITY; MODEL;
D O I：
10.1111/ijag.12191
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Thermal properties of ternary glass-forming systems within the known CaO-Al2O3-SiO2 system were evaluated. Different glass compositions near the lowest eutectic composition (around a liquidus temperature of 1170 degrees C) within the CaO-Al2O3-SiO2 system were melted from pure raw materials. The investigated target range of compositions in wt% was between 60.5 and 63.5 SiO2, 13.1 and 16.1 Al2O3, and 21.4 and 25.4 CaO. The chemical compositions, the glass transition temperatures, and the temperatures attributed to viscosities of 10(3) dPa*s were determined experimentally. It was of special interest to obtain information of all these properties of the glasses and the effect of small composition changes hereon. The liquidus temperature changed less than expected for a composition close to the eutectic composition. Temperatures at a viscosity of 10(3) dPa*s varied between 1263 and 1363 degrees C +/- 6 degrees C. A liquidus temperature of 1157 degrees C +/- 7 degrees C (with a confidence interval of 95%) of the eutectic composition was found. The results reported here may be useful for understanding and improvement of the modeling within the CaO-Al2O3-SiO2 glass system.
引用
收藏
页码：295 / 309
页数：15
相关论文
共 50 条
[31]   Viscosity of SiO2-CaO-Al2O3 Slag with Low Silica - Influence of CaO/Al2O3, SiO2/Al2O3 Ratio [J].
Siafakas, Dimitrios ;
Matsushita, Taishi ;
Jarfors, Anders Eric Wollmar ;
Hakamada, Shinya ;
Watanabe, Masahito .
ISIJ INTERNATIONAL, 2018, 58 (12) :2180-2185
[32]   DERIVATION OF CaO-SiO2-Al2O3 SYSTEM SLAG VISCOSITY EQUATION BY GP [J].
Ri, S-C ;
Ra, J-H ;
Ryom, K-C .
JOURNAL OF MINING AND METALLURGY SECTION B-METALLURGY, 2021, 57 (03) :309-317
[33]   A Raman-Structure Model for the Viscosity of SiO2-CaO-Al2O3 System [J].
Haghdani, Shokouh ;
Tangstad, Merete ;
Einarsrud, Kristian Etienne .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2022, 53 (03) :1733-1746
[34]   Effect of B2O3 on the Melting Temperature and Viscosity of CaO-SiO2-MgO-Al2O3-TiO2-Cr2O3 Slag [J].
Ma, Jing ;
Li, Wei ;
Fu, Guiqin ;
Zhu, Miaoyong .
JOURNAL OF SUSTAINABLE METALLURGY, 2021, 7 (03) :1190-1199
[35]   Phase field simulation study of the dissolution behavior of Al2O3 into CaO-Al2O3-SiO2 slags [J].
Liu, Jingjing ;
Zou, Ji ;
Guo, Muxing ;
Moelans, Nele .
COMPUTATIONAL MATERIALS SCIENCE, 2016, 119 :9-18
[36]   Viscosity of CaO-SiO2-Al2O3-MgO-B2O3 slags [J].
Babenko A.A. ;
Istomin S.A. ;
Protopopov E.V. ;
Sychev A.V. ;
Ryabov V.V. .
Steel in Translation, 2014, 44 (02) :110-112
[37]   Influence of Al2O3 and MgO on the Viscosity and Stability of CaO-MgO-SiO2-Al2O3 Slags with CaO/SiO2=1.0 [J].
Sun, Chang-yu ;
Liu, Xiao-hong ;
Li, Jing ;
Yin, Xi-tao ;
Song, Sunny ;
Wang, Qi .
ISIJ INTERNATIONAL, 2017, 57 (06) :978-982
[38]   Melting Temperature of a Selected Area in Cao-Mgo-Al2O3-Sio2 Slag System [J].
Xu, Jifang ;
Zhang, Jieyu ;
Jie, Chang ;
Tang, Lei ;
Chou, Kuochih .
ADVANCED ENGINEERING MATERIALS, PTS 1-3, 2011, 194-196 :169-174
[39]   Viscosity of low silica CaO-5MgO-Al2O3-SiO2 slags [J].
Xu, J. -F. ;
Zeng, T. ;
Sheng, M. -Q. ;
Jie, C. ;
Wan, K. ;
Zhang, J. -Y. .
IRONMAKING & STEELMAKING, 2014, 41 (07) :486-492
[40]   Accurate Viscosity Calculation for Melts in SiO2-Al2O3-CaO-MgO Systems [J].
Gan, Lei ;
Xin, Jianjiang ;
Zhou, Yihong .
ISIJ INTERNATIONAL, 2017, 57 (08) :1303-1312
12345