Structural and optical properties of Tm:Y2O3 transparent ceramic with La2O3, ZrO2 as composite sintering aid

被引：58

作者：

Yi, Qing ^{[1
,2
]}

Zhou, Shengming ^{[1
]}

Teng, Hao ^{[1
]}

Lin, Hui ^{[1
]}

Hou, Xiaorui ^{[1
,2
]}

Jia, Tingting ^{[1
,2
]}

机构：

[1] Chinese Acad Sci, Key Lab Mat High Power Laser, Shanghai Inst Opt & Fine Mech, Shanghai 201800, Peoples R China

[2] Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2012年 / 32卷 / 02期

关键词：

Y2O3; Transparent ceramic; Sintering; Grain size; Optical properties; SPECTROSCOPIC PROPERTIES; YTTRIA CERAMICS; CONTINUOUS-WAVE; SELF-DIFFUSION; EFFICIENT; YAG; TM; PERFORMANCE; SINGLE; SINTERABILITY;

D O I：

10.1016/j.jeurceramsoc.2011.09.015

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The paper reports the use of La2O3 and ZrO2 co-doping as a composite sintering aid for the fabrication of Tm:Y2O3 transparent ceramics. Two groups of experiments were conducted for investigating the influences of composite sintering aids on the microstructures and the optical properties of Tm:Y2O3 transparent ceramics in contrast to single La3+ and single Zr4+ doped Trn:Y2O3. Samples with composite sintering aids could realize fine microstructures and good optical properties at relatively low sintering temperatures. Grain sizes around 10 mu m and transmittances close to theoretical value at wavelength of 2 mu m were achieved for the 9 at.% La3+, 3 at.% Zr4+ co-doped samples sintered at 1500-1600 degrees C. The influences of the composite sintering aids on the emission intensities and the phonon energies of Tm:Y2O3 ceramics were also investigated. Crown Copyright (C) 2011 Published by Elsevier Ltd. All rights reserved.

引用

页码：381 / 388

页数：8

共 29 条

[21]

Lu SZ, 2009, 2009 LASERS & ELECTRO-OPTICS & THE PACIFIC RIM CONFERENCE ON LASERS AND ELECTRO-OPTICS, VOLS 1 AND 2, P804

[22] Growth and characterization of Tm-doped Y2O3 single crystals [J].