Electrochemical performance of microarc oxidation films formed on AZ91D alloy in two group electrolytes

被引：0

作者：

Wang, LS ^{[1
]}

Cai, QZ ^{[1
]}

Wei, BK ^{[1
]}

Liu, QX ^{[1
]}

机构：

[1] Huazhong Univ Sci & Technol, State Key Lab Die & Mould Technol, Wuhan 430074, Peoples R China

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2005年 / 15卷 / 04期

关键词：

AZ91D alloy; electrolyte; microarc oxidation; electrochemical performance;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The phase composition and electrochemical performances of microarc oxidation(MAO) films prepared on AZ91D alloy by using step-down current method in a phosphate electrolyte (P-film) and silicate electrolyte (Si-film) were studied. The results show that P-film is mainly composed of Mg, MgAl2O4 and MgO, and Si-film is composed Of Mg2SiO4 and MgO. There clearly exists a fluoride enriched zone with the thickness of about 1 - 2 mu m for P-film and 0.7 - 1 mu m for Si-film at the MAO coating/substrate interface. The electrochemical tests show that both P-film and Si-film can enhance the corrosion resistance of AZ91D magnesium alloy significantly. The corrosion failure process of the two films in 5 % (mass fraction) NaCl solution is quite different.

引用

页码：777 / 783

页数：7

共 16 条

[11] The effects of current density on the phase composition and microstructure properties of micro-arc oxidation coating
Yang, GL
Lü, XY
Bai, YZ
Cui, HF
Jin, ZS
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 345 (1-2) : 196 - 200
[12] Plasma electrolysis for surface engineering
Yerokhin, AL
Nie, X
Leyland, A
Matthews, A
Dowey, SJ
[J]. SURFACE & COATINGS TECHNOLOGY, 1999, 122 (2-3) : 73 - 93
[13] Discharge characterization in plasma electrolytic oxidation of aluminium
Yerokhin, L
Snizhko, LO
Gurevina, NL
Leyland, A
Pilkington, A
Matthews, A
[J]. JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2003, 36 (17) : 2110 - 2120
[14] YU G, 2002, CHINESE J NONFERROUS, V12, P1088
[15] ZHANG TS, 2002, INHIBITOR
[16] Zozulin AJ., 1994, MET FINISH, V92, P39

← 1 2 →