Elastic modulus of sintered porous Ti-Si-Zr, using activation by Ti-Si mechanically alloyed powder and TiH2 powder

被引：9

作者：

Goi, K. L. S. ^{[2
,3
]}

Butler, D. L. ^{[3
,4
]}

Jarfors, A. E. W. ^{[1
]}

Yong, J. M. S.

Lim, D. C. S. ^{[3
]}

机构：

[1] KIMAB, S-11428 Stockholm, Sweden

[2] Ametek, Singapore, Singapore

[3] Nanyang Technol Univ, Singapore, Singapore

[4] Singapore Inst Mfg Technol, Singapore, Singapore

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 475卷 / 1-2期

关键词：

bulk modulus; porous biomaterial; activated sintering; mechanical alloying; Ti-Si-Zr alloy;

D O I：

10.1016/j.msea.2007.02.129

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A novel biomaterial based on Ti-Si-Zr was developed using the sintering process with a composition targeting at a bulk modulus in the same range as that of human bone, i.e. 10-30 GPa. Control of porosity should also be possible to allow for the promotion osseointegration. The sintering procedure involves the use of mechanically alloyed Ti-Si-powder, and TiH2, to promote bonding, but not consolidation. The effect of porosity on the bulk modulus using compression testing is investigated. The influence of sintering temperature, heating rate, and amount and size of the TiH2-activator on porosity are also investigated. The achievable bulk modulus was in the range of 20-55 GPa at porosity levels ranging from 16% to 54%. Porosity had a profound influence on the bulk modulus, and the choice of appropriate processing conditions enables the creation of an engineered porosity and bulk modulus primarily by varying the sintering temperature and the size of the TiH2-powder particles. (C) 2007 Published by Elsevier B.V.

引用

页码：45 / 51

页数：7

共 23 条

[1]

BOBYN JD, 1981, T 7 ANN M SOC BIOM C, P13

[2]

Breme J, 2000, ADV ENG MATER, V2, P270, DOI 10.1002/(SICI)1527-2648(200005)2:5<270::AID-ADEM270>3.0.CO

[3]

2-9

[4] THE ELASTIC CONSTANTS OF MATERIALS LOADED WITH NON-RIGID FILLERS [J].

DEWEY, JM .

JOURNAL OF APPLIED PHYSICS, 1947, 18 (06) :578-581

[5] THE DETERMINATION OF THE ELASTIC FIELD OF AN ELLIPSOIDAL INCLUSION, AND RELATED PROBLEMS [J].

ESHELBY, JD .

PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1957, 241 (1226) :376-396

[6] Structural evolution in Ti-Si alloy synthesized by mechanical alloying [J].

Gu, YW ;

Goi, LS ;

Jarfors, AEW ;

Butler, DL ;

Lim, CS .

PHYSICA B-CONDENSED MATTER, 2004, 352 (1-4) :299-304

[7] Effect of oxidation treatment and surface filming on hydrogen degassing from TiH2 [J].

Han, FS ;

Zhu, ZG ;

Gao, JC ;

Song, WH .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1998, 29 (06) :1315-1319

[8] A VARIATIONAL APPROACH TO THE THEORY OF THE ELASTIC BEHAVIOUR OF MULTIPHASE MATERIALS [J].

HASHIN, Z ;

SHTRIKMAN, S .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1963, 11 (02) :127-140

[9]

HULBERT S, 1970, AICHE MAT ENG SCI DI, P87

[10]

*I ASM, 1997, FRICT WEAR TEST SOUR

← 1 2 3 →