Effect of Ta2O5 in (Ca, Si, Ta)-doped TiO2 ceramic varistors

TiO2 varistors doped with 0.2 mol% Ca, 0.4 mol% Si and different concentrations of Ta were obtained by ceramic sintering processing at 1350 degrees C. The effect of Ta on the microstructures, nonlinear electrical behavior and dielectric properties of the (Ca, Si, Ta)-doped TiO2 ceramics were investigated. The ceramics have nonlinear coefficients of alpha = 3.0-5.0 and ultrahigh relative dielectric constants which is up to 10(4). Experimental evidence shows that small quantities of Ta2O5 improve the nonlinear properties of the samples significantly. It was found that an optimal doping composition of 0.8 mol% Ta2O5 leads to a low breakdown voltage of 14.7 V/mm, a high nonlinear constant of 4.8 and an ultrahigh electrical permittivity of 5.0 x 10(4) and tg delta = 0.66 (measured at 1 kHz), which is consistent with the highest and narrowest grain boundary barriers of the ceramics. In view of these electrical characteristics, the TiO2-0.8 mol% Ta2O5 ceramic is a viable candidate for capacitor-varistor functional devices. The characteristics of the ceramics can be explained by the effect and the maximum of the substitution of Ta5+ to Ti4+. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.