Manipulating Ce Valence in RE2Fe14B Tetragonal Compounds by La-Ce Co-doping: Resultant Crystallographic and Magnetic Anomaly

Abundant and low-cost Ce has attracted considerable interest as a prospective alternative for those critically relied Nd/Pr/Dy/Tb in the 2: 14: 1-type permanent magnets. The (Nd, Ce)(2)Fe14B compound with inferior intrinsic magnetic properties to Nd2Fe14B, however, cannot provide an equivalent magnetic performance. Since Ce valence is sensitive to local steric environment, manipulating it towards the favorable trivalent state provides a way to enhance the magnetic properties. Here we report that such a desirable Ce valence can be induced by La-Ce co-doping into [(Pr, Nd)(1-x)(La, Ce) x](2.14)Fe14B (0 < x < 0.5) compounds via strip casting. As verified by X-ray photoelectron spectroscopy results, Ce valence shifts towards the magnetically favorable Ce3+ state in the composition range of x > 0.3, owing to the codoping of large radius La3+ into 2: 14: 1 phase lattice. As a result, both crystallographic and magnetic anomalies are observed in the same vicinity of x = 0.3, above which lattice parameters a and c, and saturation magnetization M-s increase simultaneously. Over the whole doping range, 2: 14: 1 tetragonal structure forms and keeps stable even at 1250 K. This finding may shed light on obtaining a favorable Ce valence via La-Ce co-doping, thus maintaining the intrinsic magnetic properties of 2: 14: 1-type permanent magnets.