Flexible and anti-freezing quasi-solid-state zinc ion hybrid supercapacitors based on pencil shavings derived porous carbon

Aqueous zinc-ion batteries have been widely reported as promising candidates for energy storage, but the research on zinc-ion based supercapacitors or hybrid supercapacitors has received little attention and the energy storage mechanism is still controversial. Here, a high-performance zinc-ion hybrid supercapacitor is successfully demonstrated with biowaste-derived porous carbon and cheap zinc foil. Thanks to the bivalent characteristic of zinc and electric double layer capacitive nature of porous carbon, as-assembed hybrid supercapacitors can achieve high energy density of 147.0 Wh kg(-1) at 136.1 W kg(-1) and a maximum power density of 15.7 kW kg(-1) at 65.4 Wh kg(-1) together with outstanding cycling stability (92.2% capacity retention after 10000 cycles at a high current density of 10 A g(-1)). Most importantly, 61.6% of the initial capacity at 1 A g(-1) can be remained even under a mass loading as high as 17 mg cm(-2). Significantly, the phase composition of byproducts formed in Zn(CF3SO3)(2) electrolyte have been confirmed by ex-situ experimental results and theoretical calculations. Besides, when appling optimized carbon cathode into quasi-solid-state hybrid supercapacitors with a unique anti-freezing hydrogel electrolyte, this device can well service at various bending states and relatively low temperature of -15 -degrees.