XRD and TEM analysis on the Fe3Al/18-8 stainless steel diffusion bonded interface

被引：11
作者：
Wang, J [1 ]
Li, YJ
Liu, P
机构：
[1] Shandong Univ, Sch Mat Sci & Engn, Minist Educ, Key Lab Liquid Struct & Hered Mat, Jinan 250061, Peoples R China
[2] Harbin Inst Technol, Natl Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
MATERIALS LETTERS | 2003年 / 57卷 / 26-27期
关键词：
Fe3Al intermetallic; diffusion; interface; phase; microstructure;
D O I：
10.1016/S0167-577X(03)00311-2
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fc(3)Al intermetallic and 18-8 stainless steel were diffusion-bonded at 1040 degreesC for 60 min. The reacted phase in the Fe3Al/18-8 diffusion-bonded interface was determined via X-ray diffractometry (XRD) and the lattice orientation relation between constituent phases was analyzed by transmission electron microscope (TEM). The results indicated that there were Fe3Al, Ni-3 Al, FeAl, alpha-Fe (Al) solid solution and Fe3C in the interface. In addition, the lattice orientation relation between alpha-Fe (Al) and Fe3C was (002)(alpha-Fe) ((Al))//(130)Fe3C. But there were no other brittle phases and micro-defects such as pore and crack, which can ensure the microstructure performance in the Fe3Al/18-8 diffusion-bonded interface. (C) 2003 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：4323 / 4327
页数：5
相关论文
共 31 条
  • [21] Microstructure and performance in diffusion-welded joints of Fe3Al/Q235 carbon steel
    Wang, J
    Li, YL
    Liu, P
    Wu, HQ
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 145 (03) : 294 - 298
  • [22] Phase constitution near the interface zone of diffusion bonding for Fe3Al/Q235 dissimilar materials
    Li, YJ
    Wang, J
    Yin, YS
    Wu, HQ
    SCRIPTA MATERIALIA, 2002, 47 (12) : 851 - 856
  • [23] Characterization of Interface in Diffusion Bonded Al2O3-TiC/Q235 Carbon Steel Dissimilar Materials
    Huang, Wanqun
    Li, Yajiang
    Wang, Juan
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2022, 75 (09) : 2419 - 2426
  • [24] Characterization of Interface in Diffusion Bonded Al2O3–TiC/Q235 Carbon Steel Dissimilar Materials
    Wanqun Huang
    Yajiang Li
    Juan Wang
    Transactions of the Indian Institute of Metals, 2022, 75 : 2419 - 2426
  • [25] Bond Interface Analysis and Creep Behavior of Vacuum Diffusion Bonded P92 Steel and 316L Austenitic Stainless Steel
    Sharma, Gaurav
    Dwivedi, Dheerendra Kumar
    Sharma, Pratishtha
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2025, 78 (03)
  • [26] Interface characteristics of Al2O3-TiC/Cr18-Ni8 diffusion-bonded joint using a Ti/Cu/Ti multi-interlayer
    Huang, W. Q.
    Li, Y. J.
    Wang, J.
    Jiang, Q. L.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2010, 48 (04): : 271 - 275
  • [27] Microstructure and composition characteristics of transition zone in diffusion bonding of Fe3Al intermetallics to Q235 low carbon steel
    Wu, HQ
    Feng, JC
    Li, YJ
    Wang, J
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 : 30 - 33
  • [28] Evaluation of interface microstructure and mechanical properties of the diffusion bonded joints of Ti-6Al-4V alloy to micro-duplex stainless steel
    Kundu, S.
    Sam, S.
    Chatterjee, S.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (15): : 4910 - 4916
  • [29] Structure and properties correlation of diffusion bonded joint of duplex stainless steel and Ti-6Al-4V with and without Ni-17Cr-9Fe alloy interlayer
    Kundu, Sukumar
    Thirunavukarasu, Gopinath
    WELDING IN THE WORLD, 2016, 60 (04) : 793 - 811
  • [30] Structure and properties correlation of diffusion bonded joint of duplex stainless steel and Ti–6Al–4V with and without Ni–17Cr–9Fe alloy interlayer
    Sukumar Kundu
    Gopinath Thirunavukarasu
    Welding in the World, 2016, 60 : 793 - 811
1234