NiAl/Ni3Al-Al2O3composite formation by reactive ball milling

被引：17

作者：

Wieczorek-Ciurowa, K ^{[1
]}

Gamrat, K ^{[1
]}

机构：

[1] Krakow Tech Univ, Inst Inorgan Chem & Technol, PL-31155 Krakow, Poland

来源：

JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY | 2005年 / 82卷 / 03期

关键词：

aluminides; aluminium; high-energy ball milling; in situ reactions; mechanical alloying; nanocomposite; Ni-Al intermetallics; Ni-hydroxycarbonate;

D O I：

10.1007/s10973-005-0955-4

中图分类号：

O414.1 [热力学];

学科分类号：

摘要：

It has been presented that the bulk mechanical alloying occurring in the Ni-hydroxycarbonate-aluminium mixture can produce homogeneously refined composite of nickel aluminides with aluminium oxide. The control of mechanochemical phenomenon was carried out by phase identification of milling products as well as their structural and morphological characterization. As a result the thermoanalytical and X-ray powder diffraction measurements as well as scanning electron microscopy with backscattered electron images (BSE) and X-ray energy dispersive spectroscopy (EDS) were applied. It was found that the kinetics of mechanochemical reactions depends on the chemical nature of initial salt.

引用

页码：719 / 724

页数：6

共 29 条

[1] Oxidation of NiAl/Al2O3 composites for controlled development of surface layers and toughening [J].

Abe, O ;

Ohwa, Y .

SOLID STATE IONICS, 2004, 172 (1-4) :553-556

[2]

[Anonymous], 2001, RUSS CHEM REV+, DOI DOI 10.1070/RC2001V070N01ABEH000598

[3] Comparison between the microstructural evolutions of two modes of SHS of NiAl: key to a common reaction mechanism [J].

Biswas, A ;

Roy, SK .

ACTA MATERIALIA, 2004, 52 (02) :257-270

[4]

BOTTA WJ, 2004, SCRIPTA MATER, V44, P1735

[5] Effect of surface grinding on the strength of NiAl and Al2O3/NiAl composites [J].

Chang, ST ;

Tuan, WH ;

You, HC ;

Lin, IC .

MATERIALS CHEMISTRY AND PHYSICS, 1999, 59 (03) :220-224

[6] Physical metallurgy of nickel aluminides [J].

Dey, GK .

SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES, 2003, 28 (1-2) :247-262

[7] Microstructural development in dispersion strengthened NiAl produced by mechanical alloying and secondary recrystallization [J].

Grahle, P ;

Arzt, E .

ACTA MATERIALIA, 1997, 45 (01) :201-211

[8] Mechanosynthesis of nanocomposites [J].

Grigorieva, TF ;

Barinova, AP ;

Lyakhov, NZ .

JOURNAL OF NANOPARTICLE RESEARCH, 2003, 5 (5-6) :439-453

[9]

GUO W, 1990, J MATER SCI, V26, P6190

[10]

HANSEN H, 1958, CONSTITUTION BINARY

← 1 2 3 →