Effect of microstructure on the corrosion behavior of a zinc-aluminium alloy

被引：17

作者：

Choudhury, P ^{[1
]}

Das, S ^{[1
]}

机构：

[1] Indian Inst Technol, Dept Met & Mat Engn, Kharagpur 721302, W Bengal, India

来源：

JOURNAL OF MATERIALS SCIENCE | 2005年 / 40卷 / 03期

关键词：

Polymer; Aluminium; Microstructure; Zinc; Aluminium Alloy;

D O I：

10.1007/s10853-005-6329-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of Ni, Ti and Sr addition on the corrosion behavior of a zinc-aluminum alloy in the die cast condition. The Immersion corrosion and the potentiodynamic polarization tests were carried out at room temperature to study the corrosion behavior. The Ni-containing alloys consisted of Ni-based intermetallic particles whose morphology changed from blocky to rod-shape with increasing Ni content. The addition of Ti resulted in rosette-shaped dendrites whereas that of Sr resulted in dendrites with increased curvature. It was observed that the addition of ni results in improved wear behavior of the alloy.

引用

页码：805 / 807

页数：3

共 10 条

[1] [Anonymous], G3172 ASTM
[2] BANERJEE SN, 1985, INTRO SCI CORROSION
[3] BELISLE S, 1986, P 25 ANN C MET CAN I, P109
[4] Effect of Ni on the wear behavior of a zinc-aluminum alloy
Choudhury, P
Das, S
Datta, BK
[J]. JOURNAL OF MATERIALS SCIENCE, 2002, 37 (10) : 2103 - 2107
[5] CHOUDHURY P, IN PRESS MAT SCI TEC
[6] Fontana M.G., 1986, Corrosion Engineering, V3rd
[7] KUBEL EJ, 1987, ADV MATER PROCESS, V132, P51
[8] MURRAY JL, 1990, BINARY ALLOY PHASE D, V1, P239
[9] Characterization of the wear response of a modified zinc-based alloy vis-a-vis a conventional zinc-based alloy and a bearing bronze at a high sliding speed
Prasad, BK
Patwardhan, AK
Yegneswaran, AH
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (11): : 3513 - 3523
[10] Shreir L.L., 1994, CORROSION

← 1 →