Study on the new friction stir spot weld joint reinforcement technique on 5754 aluminum alloy

被引：16

作者：

Andalib, Hossein ^{[1
]}

Farahani, Mohammadreza ^{[1
]}

Enami, Moeen ^{[1
]}

机构：

[1] Univ Tehran, Coll Engn, Sch Mech Engn, Kargar Shomali Ave, Tehran 1439957131, Iran

来源：

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE | 2018年 / 232卷 / 17期

关键词：

Friction stir welding; spot welding; keyhole; aluminum alloy; shear-tensile strength; MECHANICAL-PROPERTIES; PROCESS PARAMETERS; RESIDUAL-STRESSES; STATIC STRENGTH; TOOL GEOMETRY; CRACK BEHAVIOR; MICROSTRUCTURE; SHEETS;

D O I：

10.1177/0954406217729419

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this study, new friction stir spot welding method was developed using two different tools in order to create a spot weld without keyhole. The effects of process parameters and tool geometry were considered to improve the weld joint properties. The shear-tensile tests and microstructure study showed that the new method could offer superior performance in comparison to conventional friction stir spot welding. By controlling the process parameters, spot welds with strength about 37% higher than the conventional friction stir spot welds were obtained. The stir zone grain size of the prepared samples in the optimum welding conditions was decreased about four times than the base metal. It was observed that the tool plunge depth in both welding and refilling steps play a key role in creating a sound high strength welded joint. The failure load of the spot welds manufactured by concave shoulder was found to be about 7% higher than the failure load of the prepared spot welds by the flat shoulder.

引用

页码：2976 / 2986

页数：11

共 27 条

[1] Development of friction stir spot welding using rotating tool without probe and its application to low-carbon steel plates [J].

Hitachi Ltd., Tokyo, Japan ;

不详 .

Weld. Int., 2009, 8 (572-580) :572-580

[2] Effect of tool geometry on hook formation and static strength of friction stir spot welded aluminum 5754-O sheets [J].

Badarinarayan, H. ;

Shi, Y. ;

Li, X. ;

Okamoto, K. .

INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE, 2009, 49 (11) :814-823

[3] Effect of tool geometry on static strength of friction stir spot-welded aluminum alloy [J].

Badarinarayan, H. ;

Yang, Q. ;

Zhua, S. .

INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE, 2009, 49 (02) :142-148

[4]

Badarinarayan H, 2009, FUNDAMENTALS FRICTIO

[5] Material Interactions in a Novel Pinless Tool Approach to Friction Stir Spot Welding Thin Aluminum Sheet [J].

Bakavos, Dimitrios ;

Chen, Yingchun ;

Babout, Laurent ;

Prangnell, Phil .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (05) :1266-1282

[6] Influence of tool geometry and process parameters on macrostructure and static strength in friction stir spot welded polyethylene sheets [J].

Bilici, Mustafa Kemal ;

Yukler, Ahmet Irfan .

MATERIALS & DESIGN, 2012, 33 :145-152

[7] Influences of tool pin profile and welding speed on the formation of friction stir processing zone in AA2219 aluminium alloy [J].

Elangovan, K. ;

Balasubramanian, V. .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 200 (1-3) :163-175

[8] Effect of residual stresses on crack behaviour in single edge bending specimens [J].

Farahani, M. ;

Sattari-Far, I. ;

Akbari, D. ;

Alderliesten, R. .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2013, 36 (02) :115-126

[9] Effects of residual stresses on crack-tip constraints [J].

Farahani, M. ;

Sattari-Far, I. .

SCIENTIA IRANICA, 2011, 18 (06) :1267-1276

[10] Numerical and experimental investigations of effects of residual stresses on crack behavior in Aluminum 6082-T6 [J].

Farahani, Mohammadreza ;

Sattari-Far, Iradj ;

Akbari, Davood ;

Alderliesten, Rene .

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 2012, 226 (C9) :2178-2191

← 1 2 3 →