Nanocasting synthesis of ordered mesoporous alumina with crystalline walls: influence of aluminium precursors and filling times

被引：0

作者：

Liu, Qian ^{[1
]}

Wang, Aiqin ^{[1
]}

Wang, Xiaodong ^{[1
]}

Zhang, Tao ^{[1
]}

机构：

[1] Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Peoples R China

来源：

FROM ZEOLITES TO POROUS MOF MATERIALS: THE 40TH ANNIVERSARY OF INTERNATIONAL ZEOLITE CONFERENCE, PROCEEDINGS OF THE 15TH INTERNATIONAL ZEOLITE CONFERENCE | 2007年 / 170卷

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The influence of aluminum precursors and filling times on the nanocasting synthesis of ordered crystalline mesoporous alumina molecular sieve with CMK-3 as an exotemplate was investigated. With the aid of nitrogen physisorption, XRD and TEM characterizations, we found that neither aluminum alkoxide nor boehmite sol was suited to be incorporated into the template pores to achieve stable alumina frameworks under our experimental conditions. The employment of aluminum nitrate as a precursor and then in situ precipitation into the template pores led to stable alumina frameworks after 4 repeated filling cycles. Direct decomposition of alumina nitrate can also yield ordered mesoporous alumina but with poor crystallized walls.

引用

页码：1819 / 1826

页数：8

共 15 条

[1] Organized mesoporous alumina: synthesis, structure and potential in catalysis [J].

Cejka, J .

APPLIED CATALYSIS A-GENERAL, 2003, 254 (02) :327-338

[2] Formation mechanism of porous single-crystal Cr2O3 and Co3O4 templated by mesoporous silica [J].

Dickinson, Calum ;

Zhou, Wuzong ;

Hodgkins, Robert P. ;

Shi, Yifeng ;

Zhao, Dongyuan ;

He, Heyong .

CHEMISTRY OF MATERIALS, 2006, 18 (13) :3088-3095

[3] General synthesis of mesoporous spheres of metal oxides and phosphates [J].

Dong, AG ;

Ren, N ;

Tang, Y ;

Wang, YJ ;

Zhang, YH ;

Hua, WM ;

Gao, Z .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2003, 125 (17) :4976-4977

[4] Ordered mesoporous Fe2O3 with crystalline walls [J].

Jiao, F ;

Harrison, A ;

Jumas, JC ;

Chadwick, AV ;

Kockelmann, W ;

Bruce, PG .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2006, 128 (16) :5468-5474

[5] Synthesis of new, nanoporous carbon with hexagonally ordered mesostructure [J].

Jun, S ;

Joo, SH ;

Ryoo, R ;

Kruk, M ;

Jaroniec, M ;

Liu, Z ;

Ohsuna, T ;

Terasaki, O .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2000, 122 (43) :10712-10713

[6] Thermally stable nanocrystalline γ-alumina layers with highly ordered 3D mesoporosity [J].

Kuemmel, M ;

Grosso, D ;

Boissière, U ;

Smarsly, B ;

Brezesinski, T ;

Albouy, PA ;

Amenitsch, H ;

Sanchez, C .

ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2005, 44 (29) :4589-4592

[7]

LIU Q, MICROPOROUS IN PRESS

[8] Ordered crystalline alumina molecular sieves synthesized via a nanocasting route [J].

Liu, Qian ;

Wang, Aiqin ;

Wang, Xiaodong ;

Zhang, Tao .

CHEMISTRY OF MATERIALS, 2006, 18 (22) :5153-5155

[9] Mesoporous γ-alumina synthesized by hydro-carboxylic acid as structure-directing agent [J].

Liu, Qian ;

Wang, Aiqin ;

Wang, Xiaodong ;

Zhang, Tao .

MICROPOROUS AND MESOPOROUS MATERIALS, 2006, 92 (1-3) :10-21

[10] Synthesis of mesoporous magnesium oxide by CMK-3 carbon structure replication [J].

Roggenbuck, Jan ;

Koch, Guenter ;

Tiemann, Michael .

CHEMISTRY OF MATERIALS, 2006, 18 (17) :4151-4156

← 1 2 →