Influence of particle size and volume fraction on damage and fracture in Al-Al3Ti composites and micromechanical modelling using the GTN model

被引：0

作者：

He, R ^{[1
]}

Steglich, D ^{[1
]}

Heerens, J ^{[1
]}

Wang, GX ^{[1
]}

Brocks, W ^{[1
]}

Dahms, M ^{[1
]}

机构：

[1] GKSS Forschungszentrum Geesthacht GmbH, Inst Mat Res, D-21502 Geesthacht, Germany

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 1998年 / 21卷 / 10期

关键词：

particle fracture; void growth; particle distance; particle volume fraction; micromechanical modelling; Gurson model;

D O I：

暂无

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Six different Al Al3Ti composites were prepared via the powder metallurgy route. The size and volume fraction of Al3Ti particles was varied for a systematic investigation of fracture behaviour. The dominant failure mechanism in the composites is particle fracture and void growth starting from the broken particles. In comparison with the pure Al-matrix, an incorporation of Al3Ti particles reduces the crack initiation toughness and reduces the slope of the crack growth resistance curve. The inter-particle distance was found to be the main microstructural parameter controlling the slope of the crack growth resistance curve. The modified Gurson-Tvergaard-Needleman model (GTN model) was applied to one of the composites. The behaviour of tensile specimens could be successfully modelled, whereas the experimentally observed crack propagation in precracked single edge bend specimens [SE(B)] could not be simulated with the GTN model.

引用

页码：1189 / 1201

页数：13

共 22 条

[1] FORMATION OF CAVITIES FROM NON-DEFORMABLE 2ND-PHASE PARTICLES IN LOW-TEMPERATURE DUCTILE FRACTURE
ARGON, AS
[J]. JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1976, 98 (01): : 60 - 68
[2] DUCTILE FRACTURE OF A 508-CL-3 STEEL IN RELATION WITH INCLUSION CONTENT - THE BENEFIT OF THE LOCAL APPROACH OF FRACTURE AND CONTINUUM DAMAGE MECHANICS
BATISSE, R
BETHMONT, M
DEVESA, G
ROUSSELIER, G
[J]. NUCLEAR ENGINEERING AND DESIGN, 1987, 105 (01) : 113 - 120
[3] Brocks W., 1995, ASTM STP, P232
[4] VOID NUCLEATION EFFECTS IN BIAXIALLY STRETCHED SHEETS
CHU, CC
NEEDLEMAN, A
[J]. JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1980, 102 (03): : 249 - 256
[5] Clyne T.W., 1993, INTRO METAL MATRIX C
[6] *ESIS, 1992, P292 ESIS
[7] CONTINUUM THEORY OF DUCTILE RUPTURE BY VOID NUCLEATION AND GROWTH .1. YIELD CRITERIA AND FLOW RULES FOR POROUS DUCTILE MEDIA
GURSON, AL
[J]. JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1977, 99 (01): : 2 - 15
[8] MICROMECHANICAL FRACTURE PROCESS OF SIC-PARTICLE-REINFORCED ALUMINUM-ALLOY 6061-T6 METAL MATRIX COMPOSITES
KIM, HJ
KOBAYASHI, T
YOON, HS
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1992, 154 (01): : 35 - 41
[9] KIRK MT, 1993, J TEST EVAL, V21, P228, DOI 10.1520/JTE11948J
[10] A STUDY OF THE INTERNAL PARAMETERS OF DUCTILE DAMAGE THEORY
LI, ZH
BILBY, BA
HOWARD, IC
[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (09) : 1075 - 1087

← 1 2 3 →