Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water

被引：74
|
作者：
Peng, Qunjia [1 ,2 ]
Xue, He [3 ]
Hou, Juan [1 ]
Sakaguchi, Kazuhiko [1 ]
Takeda, Yoichi [1 ]
Kuniya, Jiro [1 ]
Shoji, Tetsuo [1 ]
机构：
[1] Tohoku Univ, Fracture & Reliabil Res Inst, Grad Sch Engn, Aoba Ku, Sendai, Miyagi 9808579, Japan
[2] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
[3] Xian Univ Sci & Technol, Sch Mech Engn, Xian 710054, Peoples R China
来源：
CORROSION SCIENCE | 2011年 / 53卷 / 12期
关键词：
Low alloy steel; Alloy; SEM; TEM; Stress corrosion; Welding; ENVIRONMENTALLY-ASSISTED CRACKING; NICKEL-BASE ALLOYS; STAINLESS-STEEL; SUSCEPTIBILITY; PROPERTY;
D O I：
10.1016/j.corsci.2011.08.046
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-low alloy steel (LAS) dissimilar weld joint in 288 C water was investigated by experiments and finite element simulation. Creviced bent beam and crack growth rate (CGR) experiments showed that, while the FB was a barrier to SCC growth, further crack growth into LAS was activated by a combined effect of sulfate and dissolved oxygen in water. Finite element simulation suggested that a positive gradient of hardness as the crack approached to the FB in dilution zone caused decreased CGR. Role of microstructure and water chemistry in SCC was discussed. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：4309 / 4317
页数：9
相关论文
共 50 条
  • [21] Stress corrosion cracking initiation and short crack growth behaviour in Alloy 182 weld metal under simulated boiling water reactor hydrogen water chemistry conditions
    Bai, Juxing
    Ritter, Stefan
    Seifert, Hans-Peter
    Virtanen, Sannakaisa
    CORROSION SCIENCE, 2018, 131 : 208 - 222
  • [22] Effects of water chemistry on stress corrosion cracking of 316NG weld metals in high temperature water
    Lu, Z. P.
    Shoji, T.
    Takeda, Y.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2015, 50 (01) : 41 - 48
  • [23] AN INVESTIGATION INTO STRESS CORROSION CRACKING OF DISSIMILAR METAL WELDS WITH 304L STAINLESS STEEL AND ALLOY 82 IN HIGH TEMPERATURE PURE WATER
    Yeh, Tsung-Kuang
    Huang, Guan-Ru
    Tsai, Chuen-Horng
    Wang, Mei-Ya
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 521 - 529
  • [24] Characterization of microstructure and local deformation in 316NG weld heat-affected zone and stress corrosion cracking in high temperature water
    Lu, Zhanpeng
    Shoji, Tetsuo
    Meng, Fanjiang
    Xue, He
    Qiu, Yubing
    Takeda, Yoichi
    Negishi, Koji
    CORROSION SCIENCE, 2011, 53 (05) : 1916 - 1932
  • [25] CRACK GROWTH BEHAVIOR FOR STRESS CORROSION CRACKING OF 690 ALLOY IN HIGH TEMPERATURE WATER
    Dan Tichun
    Lue Zhanpeng
    Wang Jianqiu
    Han Enhou
    Shoji, Testuo
    Ke Wei
    ACTA METALLURGICA SINICA, 2010, 46 (10) : 1267 - 1274
  • [26] Weld Heat Input and Stress Corrosion Cracking of Alloy 182 Filler in a Pressurized Water Reactor Nuclear Reactor Coolant Environment
    Silva, G. M.
    Bracarense, A. Q.
    Schvartzman, M. M. A. M.
    CORROSION, 2011, 67 (07)
  • [27] Effect of dissolved oxygen and hydrogen on the stress corrosion cracking behavior of alloy 600 in high temperature water
    Wang, Jiamei
    Zhu, Tianyu
    Chen, Kai
    Du, Donghai
    Andresen, Peter L.
    Zhang, Lefu
    JOURNAL OF NUCLEAR MATERIALS, 2021, 543
  • [28] Stress corrosion cracking of 316L HAZ for 316L stainless steel/Inconel 52M dissimilar metal weld joint in simulated primary water
    Zhu, Ruolin
    Wang, Jianqiu
    Zhang, Litao
    Zhang, Zhiming
    Han, En-hou
    CORROSION SCIENCE, 2016, 112 : 373 - 384
  • [29] Effect of chloride and sulfate additions on corrosion of low alloy steel in high-temperature water
    Sipila, Konsta
    Bojinov, Martin
    Mayinger, Wolfgang
    Saario, Timo
    Stanislowski, Michael
    ELECTROCHIMICA ACTA, 2015, 173 : 757 - 770
  • [30] Microstructure and intergranular stress corrosion cracking susceptibility of a SA508-52M-316L dissimilar metal weld joint in primary water
    Dong, Lijin
    Peng, Qunjia
    Han, En-Hou
    Ke, Wei
    Wang, Lei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (08) : 1281 - 1292
12345