Dissolution kinetics of alumina in molten CaO-Al2O3-FetO-MgO-SiO2 oxide representing the RH slag in steelmaking process

被引:34
作者
Park, Young-Joon [1 ]
Cho, Yong-Min [1 ]
Cha, Woo-Yeol [2 ]
Kang, Youn-Bae [1 ]
机构
[1] Pohang Univ Sci & Technol, Grad Inst Ferrous Technol, Pohang 37673, Kyungbuk, South Korea
[2] POSCO, Tech Res Labs, Pohang, Kyungbuk, South Korea
关键词
absorption; alumina; CaO-Al2O3-FetO-MgO-SiO2; particle size; IN-SITU OBSERVATION; CAO-AL2O3-SIO2; SLAGS; SINTERED ALUMINA; CERAMIC SYSTEMS; MGO INCLUSIONS; SILICA MELTS; AL2O3; BEHAVIOR; PARTICLES; SAPPHIRE;
D O I
10.1111/jace.16879
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
In order to effectively remove alumina inclusions suspending in ultra-low C steel during RH process, the dissolution kinetics of alumina in molten CaO-Al2O3-FetO-MgO-SiO2 oxide was investigated. A crucible dissolution technique was used where the alumina crucible was allowed to dissolve in the slag of various conditions ((% CaO)/(% Al2O3), (% FetO), temperature). The obtained data were interpreted using a kinetic mass transport equation to obtain the mass transport coefficient (k(m)) in each condition. Increasing (% CaO)/(% Al2O3), (% FetO), and temperature increased the dissolution rate as well as the k(m) provided that the slag composition is not close to its saturation composition by alumina. In order to simulate the dissolution of alumina inclusion in the RH slag, which cannot be measured by a confocal scanning laser microscopy (CSLM) at present due to the opaqueness of the slag, the modified invariant interface approximation was employed. Along with the obtained k(m), the viscosity of slag, and a reference experiment using the CSLM, the dissolution kinetics of alumina inclusion in the FetO-containing RH slag was predicted. The time required for the dissolution of alumina inclusions from liquid steel to RH slag was discussed.
引用
收藏
页码:2210 / 2224
页数:15
相关论文
共 41 条
[21]  
MORI K, 1968, T IRON STEEL I JPN, V8, P382
[22]  
Mori K., 1976, TETSU TO HAGANE, V62, P182
[23]   Dynamic recrystallization of ferrite during warm deformation of ultrafine grained ultra-low carbon steel [J].
Murty, SVSN ;
Torizuka, S ;
Nagai, K ;
Kitai, T ;
Kogo, Y .
SCRIPTA MATERIALIA, 2005, 53 (06) :763-768
[24]  
NAKASHIMA K, 1992, TETSU TO HAGANE, V78, P1674
[25]   Dissolution behavior of Al2O3 and MgO inclusions in the CaO-Al2O3-SiO2 slags:: Formation of ring-like structure of MgAl2O4 and Ca2SiO4 around MgO inclusions [J].
Park, Jin-Hong ;
Jung, In-Ho ;
Lee, Hae-Geon .
ISIJ INTERNATIONAL, 2006, 46 (11) :1626-1634
[26]   In situ observation of the dissolution phenomena of SiC particle in CaO-SiO2-MnO slag [J].
Park, Joo Hyun ;
Park, Jin Gyun ;
Min, Dong Joon ;
Lee, Young E. ;
Kang, Youn-Bae .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2010, 30 (15) :3181-3186
[27]   DISSOLUTION IN CERAMIC SYSTEMS .2. DISSOLUTION OF ALUMINA, MULLITE, ANORTHITE, AND SILICA IN A CALCIUM-ALUMINUM-SILICATE SLAG [J].
SAMADDAR, BN ;
KINGERY, WD ;
COOPER, AR .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1964, 47 (05) :249-254
[28]   DIRECT AND INDIRECT DISSOLUTION OF SAPPHIRE IN CALCIA-MAGNESIA-ALUMINA-SILICA MELTS - DISSOLUTION KINETICS [J].
SANDHAGE, KH ;
YUREK, GJ .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (12) :3633-3642
[29]   INDIRECT DISSOLUTION OF SAPPHIRE INTO CALCIA-MAGNESIA-ALUMINA-SILICA MELTS - ELECTRON-MICROPROBE ANALYSIS OF THE DISSOLUTION PROCESS [J].
SANDHAGE, KH ;
YUREK, GJ .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (12) :3643-3649
[30]   The interaction of spherical Al2O3 particles with molten Al2O3-CaO-FeOx-SiO2 slags [J].
Soll-Morris, H. ;
Sawyer, C. ;
Zhang, Z. T. ;
Shannon, G. N. ;
Nakano, J. ;
Sridhar, S. .
FUEL, 2009, 88 (04) :670-682