Dissolution kinetics of alumina in molten CaO-Al2O3-FetO-MgO-SiO2 oxide representing the RH slag in steelmaking process

被引:34
作者
Park, Young-Joon [1 ]
Cho, Yong-Min [1 ]
Cha, Woo-Yeol [2 ]
Kang, Youn-Bae [1 ]
机构
[1] Pohang Univ Sci & Technol, Grad Inst Ferrous Technol, Pohang 37673, Kyungbuk, South Korea
[2] POSCO, Tech Res Labs, Pohang, Kyungbuk, South Korea
关键词
absorption; alumina; CaO-Al2O3-FetO-MgO-SiO2; particle size; IN-SITU OBSERVATION; CAO-AL2O3-SIO2; SLAGS; SINTERED ALUMINA; CERAMIC SYSTEMS; MGO INCLUSIONS; SILICA MELTS; AL2O3; BEHAVIOR; PARTICLES; SAPPHIRE;
D O I
10.1111/jace.16879
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
In order to effectively remove alumina inclusions suspending in ultra-low C steel during RH process, the dissolution kinetics of alumina in molten CaO-Al2O3-FetO-MgO-SiO2 oxide was investigated. A crucible dissolution technique was used where the alumina crucible was allowed to dissolve in the slag of various conditions ((% CaO)/(% Al2O3), (% FetO), temperature). The obtained data were interpreted using a kinetic mass transport equation to obtain the mass transport coefficient (k(m)) in each condition. Increasing (% CaO)/(% Al2O3), (% FetO), and temperature increased the dissolution rate as well as the k(m) provided that the slag composition is not close to its saturation composition by alumina. In order to simulate the dissolution of alumina inclusion in the RH slag, which cannot be measured by a confocal scanning laser microscopy (CSLM) at present due to the opaqueness of the slag, the modified invariant interface approximation was employed. Along with the obtained k(m), the viscosity of slag, and a reference experiment using the CSLM, the dissolution kinetics of alumina inclusion in the FetO-containing RH slag was predicted. The time required for the dissolution of alumina inclusions from liquid steel to RH slag was discussed.
引用
收藏
页码:2210 / 2224
页数:15
相关论文
共 41 条
[1]   DIFFUSION-LIMITED PHASE TRANSFORMATIONS - A COMPARISON AND CRITICAL EVALUATION OF MATHEMATICAL APPROXIMATIONS [J].
AARON, HB ;
FAINSTEIN, D ;
KOTLER, GR .
JOURNAL OF APPLIED PHYSICS, 1970, 41 (11) :4404-+
[2]   SECOND PHASE DISSOLUTION [J].
AARON, HB ;
KOTLER, GR .
METALLURGICAL TRANSACTIONS, 1971, 2 (02) :393-&
[3]   FactSage thermochemical software and databases, 2010-2016 [J].
Bale, C. W. ;
Belisle, E. ;
Chartrand, P. ;
Decterov, S. A. ;
Eriksson, G. ;
Gheribi, A. E. ;
Hack, K. ;
Jung, I. -H. ;
Kang, Y. -B. ;
Melancon, J. ;
Pelton, A. D. ;
Petersen, S. ;
Robelin, C. ;
Sangster, J. ;
Spencer, P. ;
Van Ende, M-A. .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2016, 54 :35-53
[4]   Effect of alumina content and solid phase in molten flux on dissolution of alumina [J].
Bui, AH ;
Ha, HM ;
Chung, IS ;
Lee, HG .
METALS AND MATERIALS INTERNATIONAL, 2005, 11 (04) :319-326
[5]   Dissolution behavior of alumina in mold fluxes for steel continuous casting [J].
Bui, AH ;
Ha, HM ;
Kang, YB ;
Chung, IS ;
Lee, HG .
METALS AND MATERIALS INTERNATIONAL, 2005, 11 (03) :183-190
[6]   Dissolution rate of Al2O3 into molten CaO-SiO2-Al2O3 slags [J].
Choi, JY ;
Lee, HG ;
Kim, JS .
ISIJ INTERNATIONAL, 2002, 42 (08) :852-860
[8]   In Situ Observation of the Dissolution of SiO2 Particles in CaO-Al2O3-SiO2 Slags and Mathematical Analysis of its Dissolution Pattern [J].
Feichtinger, Stefan ;
Michelic, Susanne K. ;
Kang, Youn-Bae ;
Bernhard, Christian .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2014, 97 (01) :316-325
[9]   ADVANCED SHEET STEELS FOR AUTOMOTIVE APPLICATIONS [J].
FEKETE, JR ;
STRUGALA, DC ;
YAO, Z .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1992, 44 (01) :17-21
[10]   Dissolution of ZrO2, Al2O3, MgO and MgAl2O4 particles in a B2O3 containing commercial fluoride-free mould slag [J].
Fox, AB ;
Valdez, ME ;
Gisby, J ;
Atwood, RC ;
Lee, PD ;
Sridhar, S .
ISIJ INTERNATIONAL, 2004, 44 (05) :836-845