Impact of corrosion on low-cycle fatigue degradation of reinforcing bars with the effect of inelastic buckling

被引：72
|
作者：
Kashani, Mohammad M. [1 ]
Alagheband, Peyman [2 ]
Khan, Rafid [1 ]
Davis, Sean [3 ]
机构：
[1] Univ Bristol, Dept Civil Engn, Bristol BS8 1TR, Avon, England
[2] Univ Surrey, Univ Bristol, Dept Civil Engn, Guildford GU2 5XH, Surrey, England
[3] Univ Bristol, Sch Chem, Bristol BS8 1TR, Avon, England
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2015年 / 77卷
基金：
英国工程与自然科学研究理事会;
关键词：
Low-cycle fatigue; Corrosion; Buckling; Cyclic behaviour; Reinforcing steel; STEEL BARS; BEHAVIOR; COLUMNS; PATTERN;
D O I：
10.1016/j.ijfatigue.2015.03.013
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The combined effect of inelastic buckling and chloride induced corrosion damage on low-cycle high amplitude fatigue life of embedded reinforcing bars in concrete is investigated experimentally. A total of forty-eight low-cycle fatigue tests on corroded reinforcing bars varied in percentage mass loss, strain amplitudes and buckling lengths are conducted. The failure modes and crack propagation are investigated by fractography of fracture surfaces using scanning electron microscope. The results show that the inelastic buckling, percentage mass loss and nonuniform corrosion pattern are the main parameters affecting the low-cycle fatigue life of reinforcing bars. It was found that the fatigue life of corroded reinforcing bars combined with inelastic buckling has a significant path dependency. The results show that in some cases the number of cycles to failure of corroded bars under constant amplitude fatigue test is increased. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：174 / 185
页数：12
相关论文
共 50 条
  • [31] Low-cycle fatigue properties of bimetallic steel bars after exposure to elevated temperature
    Hua, Jianmin
    Wang, Fei
    Yang, Zhengtao
    Xue, Xuanyi
    Huang, Lepeng
    Chen, Zengshun
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2021, 187
  • [32] Effect of nitriding on low-cycle fatigue properties
    Guagliano, M
    Vergani, L
    INTERNATIONAL JOURNAL OF FATIGUE, 1997, 19 (01) : 67 - 73
  • [33] Low-cycle fatigue of IN 718: Effect of waveform
    Barat, Kaustav
    Sivaprasad, S.
    Kar, Sujoy Kumar
    Tarafder, Soumitra
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (12) : 2823 - 2843
  • [34] Influence of ground motion duration on seismic behavior of RC bridge piers: The role of low-cycle fatigue damage of reinforcing bars
    Su, Junsheng
    Wu, Dianqi
    Wang, Xiaowei
    ENGINEERING STRUCTURES, 2023, 279
  • [35] The effect of temperature on low-cycle fatigue of shape memory alloy
    Iasnii, V
    Yasniy, P.
    Baran, D.
    Rudawska, A.
    FRATTURA ED INTEGRITA STRUTTURALE-FRACTURE AND STRUCTURAL INTEGRITY, 2019, 13 (50): : 310 - 318
  • [36] Transfer-Learning Prediction Model for Low-Cycle Fatigue Life of Bimetallic Steel Bars
    Xue, Xuanyi
    Wang, Fei
    Wang, Neng
    Hua, Jianmin
    Deng, Wenjie
    BUILDINGS, 2024, 14 (08)
  • [37] Effect of Corrosion on Bond Mechanism between Extremely Low-Strength Concrete and Plain Reinforcing Bars
    Goksu, Caglar
    Inci, Pinar
    Ilki, Alper
    JOURNAL OF PERFORMANCE OF CONSTRUCTED FACILITIES, 2016, 30 (03)
  • [38] Phenomenological Hysteretic Model for Steel Braces Including Inelastic Postbuckling and Low-Cycle Fatigue Prediction
    Zheng, Hua-Dong
    Fan, Jian
    JOURNAL OF STRUCTURAL ENGINEERING, 2019, 145 (06)
  • [39] Low-cycle fatigue life behaviour of BS 460B and BS B500B steel reinforcing bars
    Hawileh, R. A.
    Abdalla, J. A.
    Oudah, F.
    Abdelrahman, K.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2010, 33 (07) : 397 - 407
  • [40] A Procedure for Assessing Low-Cycle Fatigue Life of Buckling-Restrained Braces
    Li, Chao-Hsien
    Vidmar, Zac
    Saxey, Brandt
    Reynolds, Mathew
    Uang, Chia-Ming
    JOURNAL OF STRUCTURAL ENGINEERING, 2022, 148 (02)
12345