A modified Al2O3 coating process to enhance the electrochemical performance of Li(Ni1/3Co1/3Mn1/3)O2 and its comparison with traditional Al2O3 coating process

被引：100

作者：

Huang, Youyuan ^{[1
]}

Chen, Jitao ^{[1
]}

Cheng, Fuquan ^{[1
]}

Wan, Wang ^{[1
]}

Liu, Wen ^{[1
]}

Zhou, Henghui ^{[1
]}

Zhang, Xinxiang ^{[1
]}

机构：

[1] Peking Univ, Coll Chem & Mol Engn, Beijing 100871, Peoples R China

来源：

JOURNAL OF POWER SOURCES | 2010年 / 195卷 / 24期

关键词：

Lithium-ion batteries; Lithium nickel cobalt manganese oxide; Alumina coating; Modification; LITHIUM-ION TRANSFER; CATHODE MATERIALS;

D O I：

10.1016/j.jpowsour.2010.07.021

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Al2O3-modified Li(Ni1/3Co1/3Mn1/3)O-2 is synthesized by a modified Al2O3 coating process. The Al2O3 coating is carried out on an intermediate, (Ni1/3Co1/3Mn1/3)(OH)(2), rather than on Li(Ni1/3Co1/3Mn1/3)O-2. As a comparison, Al2O3-coated Li(Ni1/3Co1/3Mn1/3)O-2 also is prepared by traditional Al2O3 coating process. The effects of Al2O3 coating and Al2O3 modification on structure and electrochemical performance are investigated and compared. Electrochemical tests indicate that cycle performance and rate capability of Li(Ni1/3Co1/3Mn1/3)O-2 are enhanced by Al2O3 modification without capacity loss. Al2O3 coating can also enhance the cycle performance but cause evident capacity loss and decline of rate capability. The effect of Al2O3 coating and Al2O3 modification on kinetics of lithium-ion transfer reaction at the interface of electrode/electrolyte is investigated via electrochemical impedance spectra (EIS). The result support that the Al2O3 modification increase Li+ diffused coefficient and decrease the activation energy of Li+ transfer reaction but the traditional Al2O3 coating lead to depression of Li+ diffused coefficient and increase of activation energy. (c) 2010 Elsevier B.V. All rights reserved.

引用

页码：8267 / 8274

页数：8

共 28 条

[1] Lithium ion transfer at the interface between lithium-ion-conductive solid crystalline electrolyte and polymer electrolyte [J].

Abe, T ;

Ohtsuka, M ;

Sagane, F ;

Iriyama, Y ;

Ogumi, Z .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2004, 151 (11) :A1950-A1953

[2] Building better batteries [J].

Armand, M. ;

Tarascon, J. -M. .

NATURE, 2008, 451 (7179) :652-657

[3] LiAlO2-coated LiCoO2 as cathode material for lithium ion batteries [J].

Cao, H ;

Xia, BJ ;

Zhang, Y ;

Xu, NX .

SOLID STATE IONICS, 2005, 176 (9-10) :911-914

[4] Development of Ni-Cu-Mg-Al catalysts for the synthesis of carbon nanofibers by catalytic decomposition of methane [J].

Dussault, L. ;

Dupin, J. C. ;

Guimon, C. ;

Monthioux, M. ;

Latorre, N. ;

Ubieto, T. ;

Romeo, E. ;

Royo, C. ;

Monzon, A. .

JOURNAL OF CATALYSIS, 2007, 251 (01) :223-232

[5] Recent developments in cathode materials for lithium ion batteries [J].

Fergus, Jeffrey W. .

JOURNAL OF POWER SOURCES, 2010, 195 (04) :939-954

[6] Cathode materials: A personal perspective [J].

Goodenough, John B. .

JOURNAL OF POWER SOURCES, 2007, 174 (02) :996-1000

[7] Effect of Co content on performance of LiAl1/3-xCoxNi1/3Mn1/3O2 compounds for lithium-ion batteries [J].

Hu, Shao-Kang ;

Chou, Tse-Chuan ;

Hwang, Bing-Joe ;

Ceder, Gerbrand .

JOURNAL OF POWER SOURCES, 2006, 160 (02) :1287-1293

[8] Cycle life improvement of ZrO2-coated spherical LiNi1/3Co1/3Mn1/3O2 cathode material for lithium ion batteries [J].

Hu, Shao-Kang ;

Cheng, Geng-Hao ;

Cheng, Ming-Yao ;

Hwang, Bing-Joe ;

Santhanam, Raman .

JOURNAL OF POWER SOURCES, 2009, 188 (02) :564-569

[9] A modified ZrO2-coating process to improve electrochemical performance of Li(Ni1/3Co1/3Mn1/3)O2 [J].

Huang, Youyuan ;

Chen, Jitao ;

Ni, Jiangfeng ;

Zhou, Henghui ;

Zhang, Xinxiang .

JOURNAL OF POWER SOURCES, 2009, 188 (02) :538-545

[10] Electrodes with high power and high capacity for rechargeable lithium batteries [J].

Kang, KS ;

Meng, YS ;

Bréger, J ;

Grey, CP ;

Ceder, G .

SCIENCE, 2006, 311 (5763) :977-980

← 1 2 3 →