Effect of exposing duration on the interaction between nickel-based alloy and SiC in molten LiF-NaF-KF salt

被引：7

作者：

Xue, Wandong ^{[1
,2
]}

Yang, Xinmei ^{[1
]}

Li, Zhijun ^{[1
]}

Li, Xiaoke ^{[1
]}

Wang, Jianqiang ^{[1
]}

Ignatiev, Victor ^{[3
]}

Zhou, Xingtai ^{[1
]}

机构：

[1] Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China

[2] Univ Chinese Acad Sci, Beijing 100049, Peoples R China

[3] Kurchatov Inst, Natl Res Ctr, Moscow 123182, Russia

来源：

JOURNAL OF NUCLEAR MATERIALS | 2019年 / 515卷

基金：

上海市自然科学基金; 中国国家自然科学基金;

关键词：

Nickel; Molten salts; Ceramic; High temperature corrosion; HEAT-TRANSFER FLUIDS; MO-CR ALLOY; HASTELLOY-N; CORROSION-RESISTANCE; SILICON-CARBIDE; FLUORIDE; COMPOSITES; REACTOR; PERFORMANCE; BEHAVIOR;

D O I：

10.1016/j.jnucmat.2018.12.035

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Effect of exposing duration on the interaction between nickel-based alloy (GH3535) and SiC in molten LiF-NaF-KF (FLiNaK) salt was investigated. The coexistence of GH3535 alloy and SiC deteriorates their corrosion in molten FLiNaK salt. Ni in alloy continuously diffuses outward and reacts with corrosion products of SiC to form nickel silicides on the surface of alloy. Meanwhile, Cr in alloy continuously diffuses into salt and reacts with SiC to form chromium carbides on the surface of SiC. The thickness of the deposition layer and the corrosion region in alloy are almost linearly increasing with the increase of exposing duration. (C) 2018 Elsevier B.V. All rights reserved.

引用

页码：276 / 283

页数：8

共 33 条

[31] Corrosion of a Nickel-Based Alumina-Forming Alloy in Molten NaCl-MgCl2 at 600 °C For the Development of a Molten Salt Nuclear Reactor
Pellicot, Louis
Gruet, Nathalie
Serp, Jerome
Malacarne, Romain
Bosonnet, Sophie
Touze, Gaetan
Grzonka, Justyna
Martinelli, Laure
HIGH TEMPERATURE CORROSION OF MATERIALS, 2024, 101 (05) : 1041 - 1054
[32] High-temperature corrosion of a nickel-based alloy in a molten chloride environment - The effect of thermal and chemical purifications
Mortazavi, A.
Zhao, Y.
Esmaily, M.
Allanore, A.
Vidal, J.
Birbilis, N.
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2022, 236
[33] Corrosion-driven outward migration and growth of helium bubbles in a nickel-based alloy in high-temperature molten salt environment
Lei, Guanhong
Yang, Sida
Huang, Hefei
Huang, Qing
Liu, Renduo
Zhang, Wei
Yu, Guojun
Yan, Long
CORROSION SCIENCE, 2019, 153 : 47 - 52

← 1 2 3 4 →