Influence of melting conditions on the thermal behaviour of poly(L-lactic acid)

The influence of melting temperature and time on the thermal behaviour Of poly(L-lactic acid) (PLLA) was studied with differential scanning calorimetry (DSC). Different melting conditions were investigated at temperature ranging from 200 to 210 degrees C, and for time from 2 to 20 min. For lower-molecular-weight PLLA, a single exothermic peak could be observed at cooling rate of 2 degrees C/min, after melted at different conditions. The obtained peak temperature and degrees of crystallinity dramatically increased with an increase of melting temperature or time. During subsequent heating scans, double melting peaks could be observed, which were significantly affected by prior melting conditions. The degradation of this material in the melt and the melt/re-crystallization mechanism might be responsible for the observations above. Apart from double melting, double cold crystallization peaks were observed during heating traces for this material after fast cooling (20 degrees C/min) from the melt. Prior melting conditions could significantly influence the cold crystallization behaviour. The competition between the crystallization from the nuclei remained after cooling, and that from spontaneous nucleation might be responsible for the appearance of double peaks. Additionally, the influence of melting conditions on the thermal behaviour of PLLA was dependent on the initial molecular weight. (c) 2005 Published by Elsevier Ltd.