Effect of Temperature on Microstructure and Mechanical Properties of 316L Stainless Steel Brazed Joints

被引：4
作者：
Gu, Xiaolong [1 ]
Yang, Changjin
Chen, Zhuojun [2 ]
Wu, Chengdong [3 ]
Feng, Longlong [4 ]
机构：
[1] Key Res Lab Brazing Mat & Technol Zhejiang, Hangzhou 31011, Zhejiang, Peoples R China
[2] Shenyang Ligong Univ, Sch Automot & Transportat, Shenyang, Peoples R China
[3] Shenyang Ligong Univ, Sch Mat, Shenyang, Peoples R China
[4] Shenyang Ligong Univ, Sch Mech Engn, Shenyang, Peoples R China
来源：
MATERIALS PROCESSING TECHNOLOGY, PTS 1-3 | 2012年 / 418-420卷
关键词：
NiCrP Solder; Vacuum Brazing; Brazing Temperature; Weld Seam Microstructure;
D O I：
10.4028/www.scientific.net/AMR.418-420.1494
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of brazing temperature on microstructure and mechanical properties of vacuum brazed joints of 316L stainless steel were studied. Choose three soldering temperature. After soldering, observed the microstructure, element distribution, microhardness and shear strength of welding clearance. The results show that the welding temperature for 940 degrees C, the brazing clearance organization mainly by Ni-Cr-P phase composition. Joint performance is poor, element can't get enough spread. P element does not spread easily, mainly in the brazing clearance; Cr element can spread along the grain boundary into mother material; the ability of spread of Ni elements is less than the Cr element. While welding temperature of 970 degrees C, the shear strength is the highest, and the comprehensive performance is the best.
引用
收藏
页码：1494 / +
页数：2
相关论文
共 50 条
[21]   Bonding Characterization Between 316L and Porous Stainless Steel Pipes by Vacuum Brazing [J].
Li Yaning ;
Kang Xinting ;
Wang Jian ;
Tang Huiping .
RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (02) :474-478
[22]   Interfacial microstructure and mechanical properties of the vacuum brazed C/SiC composite and Nb joints [J].
Tian, Xiaoyu ;
Feng, Jicai ;
Shi, Junmiao ;
Liu, Yuzhang ;
Zhang, Lixia .
VACUUM, 2017, 146 :97-105
[23]   The effect of iron-based filler metal element on the properties of brazed stainless steel joints for EGR cooler applications [J].
Hong Li ;
Xu Zhang ;
Owe Mårs ;
XiaoGeng Zhao ;
Qingsong Lu ;
Zhuo Chen .
Welding in the World, 2019, 63 :263-275
[24]   The effect of iron-based filler metal element on the properties of brazed stainless steel joints for EGR cooler applications [J].
Li, Hong ;
Zhang, Xu ;
Mars, Owe ;
Zhao, XiaoGeng ;
Lu, Qingsong ;
Chen, Zhuo .
WELDING IN THE WORLD, 2019, 63 (02) :263-275
[25]   Microstructure and Mechanical Properties of Vacuum Brazed TA1 Joints with TiZrCuNi Filler Metal [J].
Liu, Dashuang ;
Li, Xionghui ;
Xu, Jianhua ;
Lu, Sheng ;
Fang, Naiwen ;
Zhang, Yuke ;
Shen, Yuanxun ;
Zhong, Sujuan ;
Long, Weiming .
RARE METAL MATERIALS AND ENGINEERING, 2025, 54 (02) :394-400
[26]   Interfacial microstructure and mechanical properties of TC4/Ti60 brazed joints [J].
Bian H. ;
Tian X. ;
Feng J. ;
Gao F. ;
Hu S. .
Hanjie Xuebao/Transactions of the China Welding Institution, 2018, 39 (05) :33-36and68
[27]   Microstructure and mechanical property of electron beam brazing and vacuum brazing joints of stainless steel [J].
Li, Junmin ;
Chen, Furong ;
Liu, Jun ;
Xie, Ruijun ;
Hu, Gang .
ADVANCES IN MATERIALS MANUFACTURING SCIENCE AND TECHNOLOGY II, 2006, 532-533 :564-+
[28]   Study on the Influences of High Temperature Treatment on the Interfacial Microstructure and Mechanical Properties of TA1/TC4 Brazed Joints [J].
Gao, Dejun ;
Wu, Shaowang ;
Yang, Shengxu ;
Zhang, Chenghao ;
Zhou, Long ;
Si, Xiaoqing ;
Li, Chun ;
Qi, Junlei ;
Cao, Jian .
Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2024, 60 (14) :109-116
[29]   Effect of tin content on the microstructure and property of brazed WC-Co/CrMo alloy steel joints [J].
Wang, Hsin-Fu ;
Chiu, Liu-Ho ;
Chang, H. .
MULTI-FUNCTIONAL MATERIALS AND STRUCTURES, PTS 1 AND 2, 2008, 47-50 :596-+
[30]   Effect of brazing temperature on interfacial microstructure and properties of Ti60/Si3N4 brazed joints [J].
Hu T. ;
Lei Y. ;
Hu S. ;
Song X. ;
Wang C. .
Hanjie Xuebao/Transactions of the China Welding Institution, 2018, 39 (08) :28-31and37
12345